To catalogue
EcoPaXX® Q-HGM24
- Chemical Family
- Polyamides
EcoPaXX® Q-HGM24 is a bio-based, high-performance polyamide (PA410) made mainly from tropical castor beans, ensuring it doesn't compete with the food chain. It offers outstanding performance with excellent chemical resistance, low moisture absorption, a very high melting point, and a high crystallization rate. The material can be processed using injection molding technology. It is heat stabilized and contains 10% glass reinforcement and 20% mineral reinforcement.
Product families
Automotive & Transportation — Automotive
- Cooling & Climate
- Exterior & Body
- Interior
- Powertrain & UTH
Other characteristics
- Brand
- EcoPaXX
- Polymer Name
- Polyamide 410 (PA 410)
- Fillers Included
- Glass Fiber, Mineral
- Glass Fiber
- Mineral
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding, Injection Molding
- Reinforcement Material
- Glass Fibers, Mineral
- Glass Fibers
- Mineral
- Markets
- Automotive & Transportation
- Technology
- Composite Materials
- Plastics
- Packaging Type
- Bags
- Boxes
- Silos
- Super Sacks
- Labeling Claims
- Bio-based
- Sustainable
- Material Features
- Heat Stabilized
- Light Weight
- Reinforcement Form
- Tape
- Unidirectional Fabric
- Certifications and Compliance
- ISO 14001
- OHSAS
- REACH (Europe)
Technical data
Table 1 of 4
21 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 8000 / 6000 | MPa | ISO 527-1/-2 |
| Tensile Modulus (120°C) | 2500 / - | MPa | ISO 527-1/-2 |
| Tensile Modulus (160°C) | 2000 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (180°C) | 1600 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (200°C) | 1400 / * | MPa | ISO 527-1/-2 |
| Stress at Break | 95 / 65 | MPa | ISO 527-1/-2 |
| Stress at Break (120°C) | 45 / - | MPa | ISO 527-1/-2 |
| Stress at Break (160°C) | 35 / * | MPa | ISO 527-1/-2 |
| Stress at Break (180°C) | 30 / * | MPa | ISO 527-1/-2 |
| Stress at Break (200°C) | 26 / * | MPa | ISO 527-1/-2 |
| Strain at Break | 2.5 / 3.6 | % | ISO 527-1/-2 |
| Strain at Break (at 120°C) | 6.3 / - | % | ISO 527-1/-2 |
Table 2 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature (10°C/min) | 250 / * | °C | ISO 11357-1/-3 |
| Temperature of Deflection Under Load (1.80 MPa) | 200 / * | °C | ISO 75-1/-2 |
| Temperature of Deflection Under Load (0.45 MPa) | 235 / * | °C | ISO 75-1/-2 |
| Coefficient of Linear Thermal Expansion (parallel) | 0.48 / * | E-4/°C | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (normal) | 0.75 / * | E-4/°C | ISO 11359-1/-2 |
Table 3 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Humidity Absorption | 1.5 / * | % | Sim. to ISO 62 |
| Density | 1340 / - | kg/m³ | ISO 1183 |
| Biobased Content | 69 / * | % (Bio C/Total C) | ASTM D6866-12 Method B |
Table 4 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Molding Shrinkage (parallel) | 0.65 / * | % | ISO 294-4 |
| Molding Shrinkage (normal) | 1.1 / * | % | ISO 294-4 |