ForTii® Care P1G6

Name: ForTii® Care P1G6
Brand: ForTii®

ForTii® Care P1G6 is a cutting-edge polyphthalamide (PPA) solution suitable for challenging applications that require high-temperature performance and strength, such as metal replacement. It offers a unique chemistry that combines high peak temperature performance with chemical resistance, making it an ideal choice for demanding applications. ForTii® Care P1G6 is processed using injection molding technology and is 30% glass reinforced. It is classified as a high-performance PPA suitable for medical-grade applications.

Product families

Applications

Healthcare & Pharma — Medical

Disposable Nonwovens

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: ForTii®
Polymer Name: Polyphthalamide (PPA)
Fillers Included: Glass Fiber
Flexural Modulus: 10500.0 - 10500.0 MPa
Processing Methods: Injection Molding
Markets: Healthcare & Pharma
Technology: Plastics
Packaging Type: Bags
Boxes
Silos
Super Sacks
Material Features: Heat Resistance
High Performance
Certifications and Compliance: ISO 14001
OHSAS
REACH (Europe)
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

61 rows

Characteristic	Value	Unit	Method
Tensile Modulus	11300 / 11500	MPa	ISO 527-1/-2
Tensile Modulus (-40°C)	11500 / -	MPa	ISO 527-1/-2
Tensile Modulus (40°C)	10800 / -	MPa	ISO 527-1/-2
Tensile Modulus (80°C)	10500 / 6200	MPa	ISO 527-1/-2
Tensile Modulus (100°C)	10000 / -	MPa	ISO 527-1/-2
Tensile Modulus (120°C)	8000 / 4600	MPa	ISO 527-1/-2
Tensile Modulus (150°C)	5000 / *	MPa	ISO 527-1/-2
Tensile Modulus (160°C)	4500 / *	MPa	ISO 527-1/-2
Tensile Modulus (180°C)	4300 / *	MPa	ISO 527-1/-2
Tensile Modulus (200°C)	4000 / *	MPa	ISO 527-1/-2
Tensile Modulus (210°C)	3900 / *	MPa	ISO 527-1/-2
Tensile Modulus (Low Thickness, 1mm) - Dry	10800	MPa	ISO 527-1/-2

Table 2 of 6

9 rows

Characteristic	Value	Unit	Method
Melting Temperature (10°C/min)	325 / *	°C	ISO 11357-1/-3
Glass Transition Temperature (at 10°C/min)	125 / *	°C	ISO 11357-1/-2
Glass Transition Temperature from DMTA (tan d)	130 / *	°C	ASTM D5026/D7028
Temperature of Deflection Under Load (1.80 MPa)	305 / *	°C	ISO 75-1/-2
Temperature of Deflection Under Load (0.45 MPa)	320 / *	°C	ISO 75-1/-2
Coefficient of Linear Thermal Expansion (parallel)	0.33 / *	E-4/°C	ASTM D696
Coefficient of Linear Thermal Expansion (normal)	0.4 / *	E-4/°C	ASTM D696
Glow Wire Flammability Index (at thickness 2 / - mm)	960 / -	°C	IEC 60695-2-12
Glow Wire Ignition Temperature (at thickness 2 / - mm)	825 / -	°C	IEC 60695-2-13

Table 3 of 6

4 rows

Characteristic	Value	Unit	Method
Volume Resistivity	>1E13 / >1E13	Ohm*m	IEC 62631-3-1
Surface Resistivity	- / >1E15	Ohm	IEC 62631-3-2
Electric Strength	35 / 35	kV/mm	IEC 60243-1
Comparative Tracking Index	600 / -	V	IEC 60112