SYNTHALAT A 090
- CASE Ingredients Functions
- Binder & Resin
- Chemical Family
- Acrylics & Acrylates
SYNTHALAT A 090 is a polyisocyanate-curing acrylic resin. Utilized in 2-pack coatings that combine cycloaliphatic polyisocyanate adducts with air and oven drying. Mostly utilized for ABS copolymers and plastic coating. It has applications in coil coatings, industrial coatings, can coatings, and metal coatings.
Product families
Applications
- Coil Coatings
- Industrial Coatings
- Metal Coatings
- Can Coatings
- Can Coatings
Product Families
- Acrylics
Other characteristics
- Brand
- SYNTHALAT
- End Uses
- 2K (2 component) Coating, Coil Coating
- Compatible Substrates & Surfaces
- Glass, Metal, Plastics
- Carrier
- Solvent-based
- Markets
- Paints & Coatings
- Printing & Packaging
- Storage
Can be stored under appropriate conditions for at least one year.
- Shelf LIfe
- 1 Year
- Cure
- Chemical Cure
- Supplied As
- 60% in xylene/butyl acetate (1:1)
- Pigmentation
In combination with cycloaliphatic polyisocyanate adducts such as IPDI-adduct T 1890 S Veba-Chemie) finishes are obtained which still have good adhesion and flexibility. Good weather resistance has been demonstrated in accelerated weathering and Florida testing.
- Technology
- CASE Ingredients
- Film Properties
SYNTHALAT A 090 is used in combination with cycloaliphatic polyisocyanate adducts such as IPDI-adduct T 1890 S Veba-Chemie) finishes are obtained which still have good adhesion and flexibility. Good weather resistance has been demonstrated in accelerated weathering and Florida testing.
- Coating End Applications
- 2K (2 component) Coating
- Coil Coating
- Properties and Fields of use
SYNTHALAT-A 090 is principally used in plastics coatings which are air- or oven-drying in combination with cycloaliphatic polyisocyanate adducts. Since it is also thinnable with white spirit at ratios of up to 1 : 0.7 it can also be used to coat plastics such as ABS copolymers without swelling.
- Compatible Substrates and Surfaces
- Glass
- Metal
- Plastics
- Mixing ratio with poly-isocyanates
Based on an equivalent reaction of the reactive groups (NCO : OH = 1 : 1) the formula below calculates the quantity of polyisocyanate to be added, relative to 100 pts/wt SYNTHALAT-A 090 (solid): 42 x 100 x 2.7 17 x NCO% 42 = molecular weight of NCO groups 17 = molecular weight of OH groups 2.7 = % hydroxyl content of SYNTHALAT-A 090, relative to non-volatile content
Technical data
Table 1 of 1
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Viscosity | 1.000-1.600 | mPas | AV-F-V005 |
| Color | max. 2 | Gardner | AV-F-F007 |
| Density | 0.99 | g/ml | AV-F-0D001 |
| Flash Point | 25.0 | °C | AV-F-f006 |
| Hydroxyl Content | 80-100 | % | AV-F-H003 |
| Hydroxyl Content | 2.7 | % | Relative to NVC |
| Non Volatile Content | 60.0 | w % | AV-F-F003 |