Akulon® GA-XLG6
- Chemical Family
- Polyamides
Akulon® GA-XLG6 is a polyamide 6 (PA 6) and polyamide copolymer that functions as a resin. The features of good UV stability, good weather stability, and UV stability make this product well-suited for applications in the automotive and transportation sectors, particularly in interior components.
Product families
Applications
- Interior
Product Families
- Polyamides
Other characteristics
- Brand
- Akulon®
- Polymer Name
- Polyamide 6 (PA 6), Polyamide Copolymer
- Polyamide 6 (PA 6)
- Polyamide Copolymer
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 8500.0 - 8500.0 MPa
- Additives Included
- UV Stabilizer
- Processing Methods
- Injection Molding
- Safety
For the safety properties of the material, we refer to our SDS which can be ordered at our sales offices. During practical operation we advise to wear personal safety protections for hand/eye/body.
- Markets
- Automotive & Transportation
- PACKAGING
Akulon® grades are supplied in airtight, moisture- proof packaging.
- Technology
- Plastics
- Packaging Type
- Bags
- Boxes
- Silos
- Super Sacks
- Material Features
- Good UV Stability
- Good Weather Stability
- UV Stabilized
- Certifications and Compliance
- ISO 14001
- OHSAS
- REACH (Europe)
- HVAC Lamellae Application Data
Akulon® PA6 allows for light weight solutions as compared to metal; Akulon® PA6 allows for reliable solutions due to high weldline performance and temperature resistance (better than PP) and to its great surface appearance (better than PA66); Akulon® PA6 allows for cost effective solutions as compared to PA66; Akulon® Ultraflow grades allow even for more cost effectiveness due to 25% cycle time advantage and due to high flowability enabling thinner walled designs
- Plastics and Elastomers End Uses
- HVAC Lamellae
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 4
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 9600 / 6500 | MPa | ISO 527-1/-2 |
| Stress at Break | 170 / 115 | MPa | ISO 527-1/-2 |
| Strain at Break | 3 / 7 | % | ISO 527-1/-2 |
| Flexural Modulus | 8500 / 5500 | MPa | ISO 178 |
| Flexural Strength | 270 / 175 | MPa | ISO 178 |
| Charpy Impact Strength (at +23°C) | 65 / 85 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength (at +23°C) | 9.5 / 12 | kJ/m² | ISO 179/1eA |
Table 2 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature (10°C/min) | 222 / * | °C | ISO 11357-1/-3 |
| Temperature of Deflection Under Load (1.80 MPa) | 196 / * | °C | ISO 75-1/-2 |
| Temperature of Deflection Under Load (0.45 MPa) | 216 / * | °C | ISO 75-1/-2 |
| Coefficient of Linear Thermal Expansion (parallel) | 0.2 / * | E-4/°C | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (normal) | 0.7 / * | E-4/°C | ISO 11359-1/-2 |
Table 3 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Humidity Absorption | 2.2 / * | % | Sim. to ISO 62 |
| Density | 1360 / - | kg/m³ | ISO 1183 |
Table 4 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Molding Shrinkage (parallel) | 0.2 / * | % | ISO 294-4 |
| Molding Shrinkage (normal) | 0.6 / * | % | ISO 294-4 |