Arnite® TZ6 280-T5.03.10
Arnite® TZ6 280-T5.03.10 is a high-performance engineering plastic that offers a combination of high strength and rigidity along with excellent processing characteristics. This material is well-suited for various applications in industries such as automotive, electrical, electronics, and consumer goods. The recommended processing technology for Arnite® TZ6 280-T5.03.10 is injection molding.
Product families
Applications
Electrical & Electronics — Parts & Components
- Housings & Enclosures
- Sensors & Actuators
Product Families
Plastics — Engineering & Specialty Polymers
- Polyesters & Copolyesters
Other characteristics
- Brand
- Arnite
- Polymer Name
- Polybutylene Terephthalate (PBT)
- Fillers Included
- Glass Ball, Glass Bead, Glass Fiber
- Glass Ball
- Glass Bead
- Glass Fiber
- Flexural Modulus
- 8700.0 - 8700.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Electrical & Electronics
- Technology
- Plastics
- OEM Standards
- General Motors
- Packaging Type
- Bags
- Boxes
- Silos
- Super Sacks
- OEM Specifications
- GM GMW16427
- Certifications and Compliance
- ISO 14001
- OHSAS
- REACH (Europe)
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
27 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 9200 | MPa | ISO 527-1/-2 |
| Tensile Modulus (-40°C) | 10800 | MPa | ISO 527-1/-2 |
| Tensile Modulus (100°C) | 3900 | MPa | ISO 527-1/-2 |
| Tensile Modulus (120°C) | 3500 | MPa | ISO 527-1/-2 |
| Tensile Modulus (160°C) | 2600 | MPa | ISO 527-1/-2 |
| Tensile Modulus (180°C) | 2200 | MPa | ISO 527-1/-2 |
| Stress at Break | 110 | MPa | ISO 527-1/-2 |
| Stress at Break (-40°C) | 145 | MPa | ISO 527-1/-2 |
| Stress at Break (100°C) | 60 | MPa | ISO 527-1/-2 |
| Stress at Break (120°C) | 50 | MPa | ISO 527-1/-2 |
| Stress at Break (160°C) | 40 | MPa | ISO 527-1/-2 |
| Stress at Break (180°C) | 30 | MPa | ISO 527-1/-2 |
Table 2 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature (10°C/min) | 225 | °C | ISO 11357-1/-3 |
| Temperature of Deflection Under Load (1.80 MPa) | 195 | °C | ISO 75-1/-2 |
| Temperature of Deflection Under Load (0.45 MPa) | 210 | °C | ISO 75-1/-2 |
| Coefficient of Linear Thermal Expansion (parallel) | 0.4 | E-4/°C | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (normal) | 0.75 | E-4/°C | ISO 11359-1/-2 |
Table 3 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity | >1E13 | Ohm*m | IEC 62631-3-1 |
Table 4 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption | 0.25 | % | Sim. to ISO 62 |
| Humidity Absorption | 0.15 | % | Sim. to ISO 62 |
| Density | 1600 | kg/m³ | ISO 1183 |
Table 5 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Volume-Flow Rate (at 250 / * °C, 2.16 / * kg) | 12 | cm³/10min | ISO 1133 |
Химическая стойкость
283 rows| Characteristic | Value | Unit |
|---|---|---|
| Other | Acetic acid (10% by mass) at 23°C | not resistant |
| Other | Acetic acid (95% by mass) at 23°C | not resistant |
| Ketones | Acetone at 23°C | limited resistant, tests necessary to verify |
| Other | Acetophenone at 23°C | resistant |
| Other | Acetylene at 23°C | resistant |
| Other | Aliphatic amines at 23°C | resistant |
| Other | Aliphatic hydrocarbons at 23°C | resistant |
| Other | Allyl alcohol at 23°C | resistant |
| Other | Aluminum acetate (saturated) at 23°C | resistant |
| Other | Aluminum hydroxide (saturated) at 23°C | resistant |
| Other | Aluminum salts of mineral acids (saturated) at 23°C | resistant |
| Other | Amino acids (saturated) at 23°C | resistant |