Arnite® TZ6 280 (BK22003)
Arnite® TZ6 280 (BK22003) is a high-performance engineering plastic that offers an excellent balance of strength, rigidity, and processing characteristics. It is suitable for various applications in industries such as automotive, electrical, electronics, and consumer goods. The recommended processing technology for Arnite® TZ6 280 (BK22003) is injection molding.
Product families
Applications
Electrical & Electronics — Parts & Components
- Housings & Enclosures
- Sensors & Actuators
Product Families
Plastics — Engineering & Specialty Polymers
- Polyesters & Copolyesters
Other characteristics
- Brand
- Arnite
- Polymer Name
- Polybutylene Terephthalate (PBT)
- Fillers Included
- Glass Ball, Glass Bead, Glass Fiber
- Glass Ball
- Glass Bead
- Glass Fiber
- Flexural Modulus
- 8800.0 - 8800.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Electrical & Electronics
- Technology
- Plastics
- Packaging Type
- Bags
- Boxes
- Silos
- Super Sacks
- Certifications and Compliance
- ISO 14001
- OHSAS
- REACH (Europe)
- Plastics and Elastomers End Uses
- Actuator Covers
- Plastics and Elastomers Functions
- Resin
- Actuator Covers Application Data
Arnite® T PBT allow for light weight solutions in comparison with metal. Arnite® T PBT allow for reliable solutions due to its good dimensional stability and its good ESD performance (special Arnite® T grades)
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 9100 | MPa | ISO 527-1/-2 |
| Stress at Break | 100 | MPa | ISO 527-1/-2 |
| Strain at Break | 2.5 | % | ISO 527-1/-2 |
| Flexural Modulus | 8800 | MPa | ISO 178 |
| Flexural Strength | 160 | MPa | ISO 178 |
| Charpy Impact Strength (at +23°C) | 35 | kJ/m² | ISO 179/1eU |
| Charpy Impact Strength (at -30°C) | 30 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength (at +23°C) | 7 | kJ/m² | ISO 179/1eA |
| Charpy Notched Impact Strength (at -30°C) | 5.5 | kJ/m² | ISO 179/1eA |
Table 2 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature (10°C/min) | 225 | °C | ISO 11357-1/-3 |
| Temperature of Deflection Under Load (1.80 MPa) | 205 | °C | ISO 75-1/-2 |
| Temperature of Deflection Under Load (0.45 MPa) | 210 | °C | ISO 75-1/-2 |
| Coefficient of Linear Thermal Expansion (parallel) | 0.3 | E-4/°C | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (normal) | 1.3 | E-4/°C | ISO 11359-1/-2 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity | >1E13 | Ohm*m | IEC 62631-3-1 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
Table 4 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption | 0.25 | % | Sim. to ISO 62 |
| Humidity Absorption | 0.15 | % | Sim. to ISO 62 |
| Density | 1630 | kg/m³ | ISO 1183 |
Table 5 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Molding Shrinkage (parallel) | 0.4 | % | ISO 294-4 |
| Molding Shrinkage (normal) | 1 | % | ISO 294-4 |
Химическая стойкость
283 rows| Characteristic | Value | Unit |
|---|---|---|
| Other | Acetic acid (10% by mass) at 23°C | not resistant |
| Other | Acetic acid (95% by mass) at 23°C | not resistant |
| Ketones | Acetone at 23°C | limited resistant, tests necessary to verify |
| Other | Acetophenone at 23°C | resistant |
| Other | Acetylene at 23°C | resistant |
| Other | Aliphatic amines at 23°C | resistant |
| Other | Aliphatic hydrocarbons at 23°C | resistant |
| Other | Allyl alcohol at 23°C | resistant |
| Other | Aluminum acetate (saturated) at 23°C | resistant |
| Other | Aluminum hydroxide (saturated) at 23°C | resistant |
| Other | Aluminum salts of mineral acids (saturated) at 23°C | resistant |
| Other | Amino acids (saturated) at 23°C | resistant |