LIOPUR 2004-151
- CASE Ingredients Functions
- Binder & Resin
- Chemical Family
- Polyurethanes (PU)
LIOPUR 2004-151 is an aqueous aliphatic polyurethane dispersion based on polycarbonate. Coatings based on LIOPUR 2004-151 form tack-free, transparent films with good surface hardness after air drying. When combined with water-emulsifiable polyisocyanates, this can be used for air-drying water-based two-pack parquet fllor varnishes because of its high abrasion resistance. It has applications in architectural coatings, wood flooring, industrial coatings, wood coatings and finishes, and other printing applications.
Properties
- Physical Form
- Dispersion
Product families
Applications
- Consumer Goods — Furniture
- Architectural Coatings
- Wood Coatings & Finishes
- Architectural Coatings
- Wood Flooring
- Furniture Coatings
- Industrial Coatings
- Other Printing Applications
Product Families
- Polyurethanes (PU)
Other characteristics
- Brand
- LIOPUR
- End Uses
- 2K (2 component) Coating
- Compatible Substrates & Surfaces
- Plastics, Wood
- Carrier
- Water
- Markets
- Building & Construction
- Consumer Goods
- Paints & Coatings
- Printing & Packaging
- Storage
LIOPUR 2004-151 consists of dispersion which should be stored in tightly closed containers, protected from frost. It contains no preservatives.
- Appearance
- Transparent to colloidal
- Cure
- Chemical Cure
- Supplied As
- 33% in water
- Technology
- CASE Ingredients
- Coating End Applications
- 2K (2 component) Coating
- Properties and Fields of use
Coatings based on Liopur 2004-151 form tack-free, transparent films with good surface hardness after air drying. Coatings based on Liopur 2004-151 have high ductility and tear strength. LIOPUR 2004-151 is used in combination with water-emulsifiable polyisocyanates, Liopur 2004-151 can be used for airdrying water-based two-pack parquet floor varnishes, because of its high abrasion resistance and for 1C and 2C wood coatings because of its good chemical resistance. Liopur 2004-151 contains isocyanate-reactive groups, and consequently our application tests have shown that a binder/curing agent ratio of 100:10 can be recommended. Two-pack systems based on Liopur 2004-151 and water-miscible polyisocyanate are characterized by the fact that the curing component can simply be manually incorporated into the base paint, so that they are suitable for DIY applications. Based on our guide formulations they have a pot life of more than 5 hours with no appreciable change in viscosity.
- Compatible Substrates and Surfaces
- Plastics
- Wood
Technical data
Table 1 of 1
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Viscosity | 10-200 | mPas | AV-F-V005 |
| Minimum Film Forming Temperature | max. 5 | °C | — |
| Non Volatile Content | 33.0 | w % | AV-F-F003 |
| Organic Solvent | approx. 8.7 | — | — |
| pH | 7.0-9.0 | — | AV-F-P001 |