Arnite® B436 SE is a high-performance engineering plastic that combines high strength and rigidity with excellent processing characteristics. As a result, it is well suited for a broad range of automotive, electrical, electronics, and consumer goods applications. The processing technology is best suited for injection molding.
Product families
Applications
Automotive & Transportation — Automotive
- Exterior & Body
Product Families
Plastics — Engineering & Specialty Polymers
- Polyesters & Copolyesters
Other characteristics
- Brand
- Arnite
- Polymer Name
- Polybutylene Terephthalate (PBT)
- Fillers Included
- Glass Fiber
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Packaging Type
- Bags
- Boxes
- Silos
- Super Sacks
- Material Features
- Flame Retardant
- Certifications and Compliance
- ISO 14001
- OHSAS
- REACH (Europe)
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 10500 | MPa | ISO 527-1/-2 |
| Stress at Break | 105 | MPa | ISO 527-1/-2 |
| Strain at Break | 1.7 | % | ISO 527-1/-2 |
| Charpy Impact Strength (at +23°C) | 45 | kJ/m² | ISO 179/1eU |
| Charpy Impact Strength (at -30°C) | 45 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength (at +23°C) | 6 | kJ/m² | ISO 179/1eA |
| Charpy Notched Impact Strength (at -30°C) | 6 | kJ/m² | ISO 179/1eA |
Table 2 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature (10°C/min) | 225 | °C | ISO 11357-1/-3 |
| Temperature of Deflection Under Load (1.80 MPa) | 210 | °C | ISO 75-1/-2 |
| Temperature of Deflection Under Load (0.45 MPa) | 220 | °C | ISO 75-1/-2 |
| Coefficient of Linear Thermal Expansion (parallel) | 0.35 | E-4/°C | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (normal) | 0.7 | E-4/°C | ISO 11359-1/-2 |
| Glow Wire Flammability Index (at thickness 1.5 / - mm) | 960 | °C | IEC 60695-2-12 |
Table 3 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Relative Permittivity (100Hz) | 4.1 | — | IEC 62631-2-1 |
| Relative Permittivity (1 MHz) | 3.9 | — | IEC 62631-2-1 |
| Dissipation Factor (100 Hz) | 20 | E-4 | IEC 62631-2-1 |
| Dissipation Factor (1 MHz) | 150 | E-4 | IEC 62631-2-1 |
| Volume Resistivity | >1E13 | Ohm*m | IEC 62631-3-1 |
| Electric Strength | 28 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
Table 4 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption | 0.3 | % | Sim. to ISO 62 |
| Humidity Absorption | 0.15 | % | Sim. to ISO 62 |
| Density | 1670 | kg/m³ | ISO 1183 |
Химическая стойкость
283 rows| Characteristic | Value | Unit |
|---|---|---|
| Other | Acetic acid (10% by mass) at 23°C | not resistant |
| Other | Acetic acid (95% by mass) at 23°C | not resistant |
| Ketones | Acetone at 23°C | limited resistant, tests necessary to verify |
| Other | Acetophenone at 23°C | resistant |
| Other | Acetylene at 23°C | resistant |
| Other | Aliphatic amines at 23°C | resistant |
| Other | Aliphatic hydrocarbons at 23°C | resistant |
| Other | Allyl alcohol at 23°C | resistant |
| Other | Aluminum acetate (saturated) at 23°C | resistant |
| Other | Aluminum hydroxide (saturated) at 23°C | resistant |
| Other | Aluminum salts of mineral acids (saturated) at 23°C | resistant |
| Other | Amino acids (saturated) at 23°C | resistant |