EcoPaXX® Q-DWX6
- Chemical Family
- Polyamides
EcoPaXX® Q-DWX6 is a long aliphatic polyamide with excellent mechanical and flow performance, suitable for food contact and drinking water applications. It offers exceptional chemical resistance, low moisture absorption, a very high melting point, and a high crystallization rate. The material can be processed using injection molding technology. It has good surface properties and meets the requirements for drinking water contact grade. It is also 30% glass-reinforced and meets the standards for food contact quality.
Other characteristics
- Brand
- EcoPaXX
- Polymer Name
- Polyamide 410 (PA 410)
- Fillers Included
- Glass Fiber
- Processing Methods
- Injection Molding, Injection Molding
- Reinforcement Material
- Glass Fibers
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Industrial
- Flame Rating
- UL 94 HB
- Technology
- Composite Materials
- Plastics
- Packaging Type
- Bags
- Boxes
- Silos
- Super Sacks
- Labeling Claims
- Bio-based
- Food Contact Acceptable
- Sustainable
- Quality Standards
- UL Yellow Card (E47960)
Technical data
Table 1 of 5
18 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 9500 / 9300 | MPa | ISO 527-1/-2 |
| Tensile Modulus (120°C) | 2800 / - | MPa | ISO 527-1/-2 |
| Tensile Modulus (140°C) | 2500 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (160°C) | 2200 / * | MPa | ISO 527-1/-2 |
| Stress at Break | 190 / 170 | MPa | ISO 527-1/-2 |
| Stress at Break (120°C) | 65 / - | MPa | ISO 527-1/-2 |
| Stress at Break (140°C) | 55 / * | MPa | ISO 527-1/-2 |
| Stress at Break (160°C) | 45 / * | MPa | ISO 527-1/-2 |
| Strain at Break | 3.3 / 3.5 | % | ISO 527-1/-2 |
| Strain at Break (at 120°C) | 15 / - | % | ISO 527-1/-2 |
| Strain at Break (at 140°C) | 14 / * | % | ISO 527-1/-2 |
| Strain at Break (at 160°C) | 13 / * | % | ISO 527-1/-2 |
Table 2 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature (10°C/min) | 250 / * | °C | ISO 11357-1/-3 |
| Temperature of Deflection Under Load (1.80 MPa) | 190 / * | °C | ISO 75-1/-2 |
| Temperature of Deflection Under Load (0.45 MPa) | 230 / * | °C | ISO 75-1/-2 |
| Burning Behaviour (at 1.5 mm Nominal Thickness) | UL HB / * | class | IEC 60695-11-10 |
| Burning Behaviour (at 3.0 mm Nominal Thickness) | UL HB / * | class | IEC 60695-11-10 |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption | 4 / * | % | Sim. to ISO 62 |
| Humidity Absorption | 1.5 / * | % | Sim. to ISO 62 |
| Density | 1350 / - | kg/m³ | ISO 1183 |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Molding Shrinkage (parallel) | 0.25 / * | % | ISO 294-4 |
| Molding Shrinkage (normal) | 0.75 / * | % | ISO 294-4 |
Химическая стойкость
377 rows| Characteristic | Value | Unit |
|---|---|---|
| Other | Acetaldehyde (40% by mass) at 23°C | resistant |
| Other | Acetamide (50% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | Acetamide (50% by mass) at >140°C | not resistant |
| Other | Acetic acid (10% by mass) at 100°C | limited resistant, tests necessary to verify |
| Other | Acetic acid (10% by mass) at 23°C | resistant |
| Other | Acetic acid (95% by mass) at 23°C | limited resistant, tests necessary to verify |
| Ketones | Acetone at 23°C | resistant |
| Other | Acetophenone at 23°C | resistant |
| Other | Acetyl chloride at 23°C | limited resistant, tests necessary to verify |
| Other | Acetylene at 23°C | resistant |
| Other | Acrylic acid at 23°C | limited resistant, tests necessary to verify |
| Other | Aliphatic amines at 23°C | resistant |