Stanyl® Diablo HDT2700 BK00001
- Chemical Family
- Polyamides
Stanyl® Diablo HDT2700 BK00001 is a high-heat polyamide that offers excellent heat resistance up to 230 °C continuous use temperature, along with high creep resistance, strength, stiffness, and fatigue resistance. Diablo HDT2700 is specifically designed for high-demand automotive underhood applications. It is a high-performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear and friction, and process flow qualities are required. This high-performance polyamide 46 is used for applications in automotive, E&E, gears, and outdoor power equipment. Since it retains its mechanical properties at high temperatures up to 220 °C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP. It is 40% glass-reinforced, heat-stabilized, and suitable for injection molding.
Product families
Applications
- Cooling & Climate
Product Families
- Polyamides
Other characteristics
- Brand
- Stanyl
- Polymer Name
- Polyamide 46 (PA 46)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 12000.0 - 12000.0 MPa
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Technology
- Plastics
- OEM Standards
- PSA
- Renault
- Packaging Type
- Bags
- Boxes
- Silos
- Super Sacks
- Material Features
- Heat Resistance
- Heat Stabilized
- High Thermo-Oxidative Stability
- OEM Specifications
- PSA Peugeot-Citroen 01994-15-00280
- RENAULT PMR
- Certifications and Compliance
- ISO 14001
- OHSAS
- REACH (Europe)
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
40 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 13500 / 7000 | MPa | ISO 527-1/-2 |
| Tensile Modulus (-40°C) | 14500 / - | MPa | ISO 527-1/-2 |
| Tensile Modulus (120°C) | 5400 / - | MPa | ISO 527-1/-2 |
| Tensile Modulus (160°C) | 5000 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (180°C) | 4500 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (200°C) | 4000 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (210°C) | 3500 / * | MPa | ISO 527-1/-2 |
| Stress at Break | 215 / 130 | MPa | ISO 527-1/-2 |
| Stress at Break (-40°C) | 280 / - | MPa | ISO 527-1/-2 |
| Stress at Break (120°C) | 105 / - | MPa | ISO 527-1/-2 |
| Stress at Break (160°C) | 85 / * | MPa | ISO 527-1/-2 |
| Stress at Break (180°C) | 75 / * | MPa | ISO 527-1/-2 |
Table 2 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature (10°C/min) | 285 / * | °C | ISO 11357-1/-3 |
| Glass Transition Temperature (at 10°C/min) | 70 / * | °C | ISO 11357-1/-2 |
| Glass Transition Temperature from DMTA (tan d) | 68 / * | °C | ASTM D5026/D7028 |
| Temperature of Deflection Under Load (1.80 MPa) | 263 / * | °C | ISO 75-1/-2 |
| Temperature of Deflection Under Load (0.45 MPa) | 275 / * | °C | ISO 75-1/-2 |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption | 5.9 / * | % | Sim. to ISO 62 |
| Humidity Absorption | 2.3 / * | % | Sim. to ISO 62 |
| Density | 1480 / - | kg/m³ | ISO 1183 |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Molding Shrinkage (parallel) | 0.5 / * | % | ISO 294-4 |
| Molding Shrinkage (normal) | 1 / * | % | ISO 294-4 |
Химическая стойкость
377 rows| Characteristic | Value | Unit |
|---|---|---|
| Other | Acetaldehyde (40% by mass) at 23°C | resistant |
| Other | Acetamide (50% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | Acetamide (50% by mass) at >140°C | not resistant |
| Other | Acetic acid (10% by mass) at 100°C | not resistant |
| Other | Acetic acid (10% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | Acetic acid (95% by mass) at 23°C | not resistant |
| Ketones | Acetone at 23°C | resistant |
| Other | Acetophenone at 23°C | resistant |
| Other | Acetyl chloride at 23°C | not resistant |
| Other | Acetylene at 23°C | resistant |
| Other | Acrylic acid at 23°C | not resistant |
| Other | Aliphatic amines at 23°C | resistant |