Stanyl® 46SF5030

Chemical Family: Polyamides

Stanyl® 46SF5030 is a high-performance polyamide known for its exceptional heat resistance, stiffness in design, wear and friction properties, and processing qualities. It finds applications in automotive, E&E, gears, and outdoor power equipment. Withstanding temperatures up to 220°C, it surpasses PPA, PA6T, PA9T, and often PPS and LCP, making it ideal for demanding high-performance uses. It is best suited for injection molding.

Product families

Applications

Electrical & Electronics — Parts & Components

Connectors

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: Stanyl
Polymer Name: Polyamide 46 (PA 46)
Fillers Included: Glass Fiber
Flexural Modulus: 11000.0 - 11000.0 MPa
Additives Included: Heat Stabilizer
Processing Methods: Injection Molding
Markets: Electrical & Electronics
Flame Rating: UL 94 V0
Technology: Plastics
Packaging Type: Bags
Boxes
Silos
Super Sacks
Quality Standards: UL Yellow Card (E47960)
Material Features: Flame Retardant
Heat Resistance
Heat Stabilized
High Flow
High Flowability
UL Flame Rated
Certifications and Compliance: ISO 14001
OHSAS
REACH (Europe)
UL 94
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 8

17 rows

Characteristic	Value	Unit	Method
Tensile Modulus	12000 / 7500	MPa	ISO 527-1/-2
Tensile Modulus (Low Thickness, 1mm)	13000 / -	MPa	ISO 527-1/-2
Stress at Break	170 / 110	MPa	ISO 527-1/-2
Stress at Break, at low thickness	180 / -	MPa	ISO 527-1/-2
Stress at Break (Thickness tested)	1 / -	mm	ISO 527-1/-2
Strain at Break	1.9 / 2.8	%	ISO 527-1/-2
Strain at Break, at low thickness	1.8 / -	%	ISO 527-1/-2
Strain at Break (Thickness tested)	1 / -	mm	ISO 527-1/-2
Flexural Modulus	11000 / 6800	MPa	ISO 178
Flexural Strength	240 / 165	MPa	ISO 178
Charpy Impact Strength (at +23°C)	40 / 40	kJ/m²	ISO 179/1eU
Charpy Notched Impact Strength (at +23°C)	13 / 13	kJ/m²	ISO 179/1eA

Table 2 of 8

19 rows

Characteristic	Value	Unit	Method
Melting Temperature (10°C/min)	295 / *	°C	ISO 11357-1/-3
Glass Transition Temperature (at 10°C/min)	75 / *	°C	ISO 11357-1/-2
Temperature of Deflection Under Load (1.80 MPa)	290 / *	°C	ISO 75-1/-2
Temperature of Deflection Under Load (0.45 MPa)	290 / *	°C	ISO 75-1/-2
Vicat Softening Temperature (50°C/h 50N)	290 / *	°C	ISO 306
Coefficient of Linear Thermal Expansion (parallel)	0.2 / *	E-4/°C	ISO 11359-1/-2
Coefficient of Linear Thermal Expansion (normal)	0.45 / *	E-4/°C	ISO 11359-1/-2
Burning Behaviour (at 1.5 mm Nominal Thickness)	UL V-0 / *	class	IEC 60695-11-10
Burning Behaviour (at 3.0 mm Nominal Thickness)	UL V-0 / *	class	IEC 60695-11-10
Glow Wire Flammability Index (at thickness 3 / - mm)	960 / -	°C	IEC 60695-2-12
Glow Wire Flammability Index (at thickness 0.75 / - mm)	960 / -	°C	IEC 60695-2-12
Glow Wire Ignition Temperature (at thickness 3 / - mm)	960 / -	°C	IEC 60695-2-13

Table 3 of 8

8 rows

Characteristic	Value	Unit	Method
Relative Permittivity (100Hz)	4.3 / -	—	IEC 62631-2-1
Relative Permittivity (1 MHz)	4 / -	—	IEC 62631-2-1
Dissipation Factor (100 Hz)	60 / -	E-4	IEC 62631-2-1
Dissipation Factor (1 MHz)	160 / -	E-4	IEC 62631-2-1
Volume Resistivity	>1E13 / 1E8	Ohm*m	IEC 62631-3-1
Surface Resistivity	- / 1E14	Ohm	IEC 62631-3-2
Electric Strength	30 / 20	kV/mm	IEC 60243-1
Comparative Tracking Index	225 / -	V	IEC 60112

Table 4 of 8

1 row

Characteristic	Value	Unit	Method
Viscosity Number	66 / *	cm³/g	ISO 307, 1157, 1628

Table 5 of 8

4 rows

Characteristic	Value	Unit
Density of Melt	1450 / *	kg/m³
Thermal Conductivity of Melt	0.258 / *	W/(m K)
Specific Heat Capacity Melt	1750 / *	J/(kg K)
Effective Thermal Diffusivity	1.01E-7 / *	m²/s

Table 6 of 8