Arnitel® XG01IS
- Chemical Family
- Polyesters
Arnitel® XG01IS is a high-performance thermoplastic copolyester (TPC) known for its distinctive blend of flexibility, high temperature resistance, and strength, along with excellent processing characteristics. In industries ranging from automotive to E&E, Arnitel® XG01IS is gaining recognition as a more sustainable and efficient alternative to traditional rubbers, resulting in reduced environmental impact and lower system costs. This material can be processed using extrusion technology, making it suitable for a wide range of applications with specific requirements.
Product families
Applications
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
Electrical & Electronics — Wire & Cable
- Power Transmission & Distribution
Product Families
Elastomers — Thermoplastic Elastomers
- Thermoplastic Polyester Elastomers (TPE-E)
Other characteristics
- Brand
- Arnitel
- Density
- 1130.0 - 1130.0 kg/m³
- Polymer Name
- Thermoplastic Copolyester Elastomer (TPC-ET)
- Strain at Break
- 350.0 - 350.0 %
- Processing Methods
- Extrusion
- Markets
- Electrical & Electronics
- Flame Rating
- UL 94 V1
- UL 94 V2
- Technology
- Elastomers
- Packaging Type
- Bags
- Boxes
- Silos
- Super Sacks
- Labeling Claims
- Halogen-free
- Quality Standards
- UL Yellow Card (E47960)
- Material Features
- Flame Retardant
- UL Flame Rated
- Certifications and Compliance
- ISO 14001
- OHSAS
- REACH (Europe)
- UL 94
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
Technical data
Table 1 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature (10°C/min) | 172 | °C | ISO 11357-1/-3 |
| Glass Transition Temperature (at 10°C/min) | -70 | °C | ISO 11357-1/-2 |
| Burning Behaviour (at 1.5 mm Nominal Thickness) | UL V-2 | class | IEC 60695-11-10 |
| Burning Behaviour (at 3.0 mm Nominal Thickness) | UL V-1 | class | IEC 60695-11-10 |
Table 2 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity | 1.9E11 | Ohm*m | IEC 62631-3-1 |
| Electric Strength | 21 | kV/mm | IEC 60243-1 |
Table 3 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption | 0.17 | % | Sim. to ISO 62 |
| Humidity Absorption | 0.45 | % | Sim. to ISO 62 |
| Density | 1130 | kg/m³ | ISO 1183 |
Table 4 of 6
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 56 | MPa | ISO 527-1/-2 |
| Stress at 10% strain | 3 | MPa | ISO 527-1/-2 |
| Stress at 100% strain | 4.4 | MPa | ISO 527-1/-2 |
| Stress at Break | 8.5 | MPa | ISO 527-1/-2 |
| Nominal Strain at Break | 350 | % | ISO 527-1/-2 |
| Shore A Hardness (3s) | 86 | — | ISO 868 |
Table 5 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Volume-Flow Rate (at 230 / * °C, 2.16 / * kg) | 2.7 | cm³/10min | ISO 1133 |
Химическая стойкость
24 rows| Characteristic | Value | Unit |
|---|---|---|
| Other | Acetic acid (10% by mass) at 23°C | resistant |
| Ketones | Acetone at 23°C | resistant |
| Other | Ammonium hydroxide (10% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | ASTM 1 at 23°C | resistant |
| Other | ASTM 3 at 23°C | resistant |
| Other | Brake fluids (DOT 3/4) at 23°C | not resistant |
| Other | Calcium chloride (10% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | Chloroform at 23°C | not resistant |
| Ethers | Diethyl ether at 23°C | limited resistant, tests necessary to verify |
| Alcohols | Ethanol at 23°C | limited resistant, tests necessary to verify |
| Other | Ethyl Acetate at 23°C | limited resistant, tests necessary to verify |
| Other | Fuel; Diesel at 85°C | resistant |