Arnitel® PB582-H

Chemical Family: Polyesters

Arnitel® PB582-H is a high-performance thermoplastic copolyester (TPC) known for its exceptional blend of flexibility, high temperature resistance, and strength, complemented by excellent processing characteristics. In industries spanning from automotive to E&E, Arnitel® PB582-H is gaining prominence as a more sustainable and efficient alternative to traditional rubbers, leading to reduced environmental impact and lower system costs. This material can be processed using blow molding technology and includes heat stabilization for enhanced performance in demanding applications.

Product families

Applications

Automotive & Transportation — Automotive

Cooling & Climate

Product Families

Elastomers — Thermoplastic Elastomers

Thermoplastic Polyester Elastomers (TPE-E)

Other characteristics

Brand: Arnitel
Density: 1230.0 - 1230.0 kg/m³
End Uses: Air Ducts
Polymer Name: Thermoplastic Copolyester Elastomer (TPC-ET)
Strain at Break: 610.0 - 610.0 %
Flexural Modulus: 310.0 - 310.0 MPa
Processing Methods: Blow Molding
Markets: Automotive & Transportation
Technology: Elastomers
OEM Standards: General Motors
PSA
Renault
Packaging Type: Bags
Boxes
Silos
Super Sacks
Additives Included: Heat Stabilizer
Material Features: Heat Stabilized
OEM Specifications: GM GMW15702-250053
GM GMW15702-250053 TPC-ET
PSA Peugeot-Citroen SPA X62 5103
RENAULT FEM 03-20-007
RENAULT PMR
Chemical Resistance: Limited resistant, tests necessary to verify
Certifications and Compliance: ISO 14001
OHSAS
REACH (Europe)
Plastics and Elastomers End Uses: Air Ducts
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Blow Molding

Technical data

Table 1 of 6

7 rows

Characteristic	Value	Unit	Method
Flexural Modulus	310	MPa	ISO 178
Flexural Modulus (at 120°C)	110	MPa	ISO 178
Charpy Impact Strength (at 23°C)	N	kJ/m²	ISO 179/1eU
Charpy Impact Strength (at -30°C)	N	kJ/m²	ISO 179/1eU
Charpy Notched Impact Strength (at 23°C)	N	kJ/m²	ISO 179/1eA
Charpy Notched Impact Strength (at -30°C)	15	kJ/m²	ISO 179/1eA
Izod Notched Impact Strength (at 23°C)	N	kJ/m²	ISO 180/1A

Table 2 of 6

3 rows

Characteristic	Value	Unit	Method
Temperature of Deflection Under Load (at 0.45 MPa)	100	°C	ISO 75-1/-2
Melting Temperature (at 10°C/min)	220	°C	ISO 11357-1/-3
Vicat Softening Temperature (at 50°C/h 50N)	105	°C	ISO 306

Table 3 of 6

1 row

Characteristic	Value	Unit	Method
Density	1230	kg/m³	ISO 1183

Table 4 of 6

10 rows

Characteristic	Value	Unit	Method
Stress (at Break, Normal)	41	MPa	ISO 527-1/-2
Stress (at 5% Strain, Normal)	11	MPa	ISO 527-1/-2
Stress (at 10% Strain, Normal)	15	MPa	ISO 527-1/-2
Stress (at 50% Strain, Normal)	17.5	MPa	ISO 527-1/-2
Stress (at 10% Strain, Parallel, 100°C)	7.1	MPa	ISO 527-1/-2
Stress (at 100% Strain, Normal)	17	MPa	ISO 527-1/-2
Strain (at Break, Normal)	610	%	ISO 527-1/-2
Stress (at 10% Strain, Parallel)	14	MPa	ISO 527-1/-2
Tear Strength (Normal)	131	kN/m	ISO 34-1; Method B
Tear Strength (Parallel)	137	kN/m	ISO 34-1; Method B

Table 5 of 6

8 rows

Characteristic	Value	Unit	Method
Tensile Modulus	300	MPa	ISO 527-1/-2
Stress (at 5% Strain)	13	MPa	ISO 527-1/-2
Stress (at 10% Strain)	18	MPa	ISO 527-1/-2
Stress (at 50% Strain)	25	MPa	ISO 527-1/-2
Stress (at 100% Strain)	28	MPa	ISO 527-1/-2
Stress (at Break)	30	MPa	ISO 527-1/-2
Nominal Strain (at Break)	150	%	ISO 527-1/-2
Hardness (3s)	55	Shore D	ISO 868

Table 6 of 6