To catalogue
Arnitel® PL420-H
- Chemical Family
- Polyesters
Arnitel® PL420-H is a high-performance thermoplastic copolyester (TPC) renowned for its exceptional blend of flexibility, high temperature resistance, and strength, complemented by excellent processing characteristics. In industries spanning from automotive to E&E, Arnitel® PL420-H is gaining prominence as a more sustainable and efficient alternative to traditional rubbers, leading to reduced environmental impact and lower system costs. This material can be processed using injection molding technology and includes heat stabilization for enhanced performance in demanding applications.
Product families
Applications
Automotive & Transportation — Automotive
- Chassis & Brake
- Exterior & Body
Product Families
Elastomers — Thermoplastic Elastomers
- Thermoplastic Polyester Elastomers (TPE-E)
Other characteristics
- Brand
- Arnitel
- Density
- 1180.0 - 1180.0 kg/m³
- End Uses
- Automotive Exterior Parts
- Polymer Name
- Thermoplastic Copolyester Elastomer (TPC-ET)
- Strain at Break
- 330.0 - 330.0 %
- Flexural Modulus
- 80.0 - 80.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Technology
- Elastomers
- OEM Standards
- Callout
- Ford
- Volkswagen
- Packaging Type
- Bags
- Boxes
- Silos
- Super Sacks
- Additives Included
- Heat Stabilizer
- OEM Specifications
- CALLOUT ASTM D6835 TEEE0310
- CALLOUT ISO 20029-TPC-ETMH38-22-008
- FORD WSS-M4D683-A2
- VW 50180
- Body Plugs Application Data
Arnitel® offers the best combination of peak temperature, flexibility and processability. Arnitel® has a proven portfolio of grades suitable for different types of bodyplugs
- Certifications and Compliance
- ISO 14001
- OHSAS
- REACH (Europe)
- Plastics and Elastomers End Uses
- Automotive Exterior Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 8
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 80 | MPa | ISO 178 |
| Charpy Impact Strength (at +23°C) | N | kJ/m² | ISO 179/1eU |
| Charpy Impact Strength (at -30°C) | N | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength (at +23°C) | N | kJ/m² | ISO 179/1eA |
| Charpy Notched Impact Strength (at -30°C) | N | kJ/m² | ISO 179/1eA |
| Izod Notched Impact Strength (at +23°C) | N | kJ/m² | ISO 180/1A |
| Izod Notched Impact Strength (at -20°C) | N | kJ/m² | ISO 180/1A |
| Izod Notched Impact Strength (at -30°C) | N | kJ/m² | ISO 180/1A |
Table 2 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature (10°C/min) | 220 | °C | ISO 11357-1/-3 |
Table 3 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity | >1E13 | Ohm*m | IEC 62631-3-1 |
Table 4 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1180 | kg/m³ | ISO 1183 |
Table 5 of 8
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Stress at Break (normal) | 13 | MPa | ISO 527-1/-2 |
| Strain at Break (normal) | 330 | % | ISO 527-1/-2 |
| Tear Strength (normal) | 105 | kN/m | ISO 34-1; Method B |
| Tear Strength (parallel) | 97 | kN/m | ISO 34-1; Method B |
Table 6 of 8
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 86 | MPa | ISO 527-1/-2 |
| Stress at 10% strain | 6 | MPa | ISO 527-1/-2 |
| Stress at 100% strain | 9.6 | MPa | ISO 527-1/-2 |
| Stress at Break | 14 | MPa | ISO 527-1/-2 |
| Nominal Strain at Break | 275 | % | ISO 527-1/-2 |
| Shore D Hardness (3s) | 38 | — | ISO 868 |
Table 7 of 8
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Volume-Flow Rate (at 230 / * °C, 2.16 / * kg) | 23 | cm³/10min | ISO 1133 |
| Molding Shrinkage (parallel) | 1.6 | % | Sim. to ISO 294-4 |
| Molding Shrinkage (normal) | 1.75 | % | Sim. to ISO 294-4 |
Химическая стойкость
24 rows| Characteristic | Value | Unit |
|---|---|---|
| Other | Acetic acid (10% by mass) at 23°C | resistant |
| Ketones | Acetone at 23°C | resistant |
| Other | Ammonium hydroxide (10% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | ASTM 1 at 23°C | resistant |
| Other | ASTM 3 at 23°C | resistant |
| Other | Brake fluids (DOT 3/4) at 23°C | not resistant |
| Other | Calcium chloride (10% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | Chloroform at 23°C | not resistant |
| Ethers | Diethyl ether at 23°C | limited resistant, tests necessary to verify |
| Alcohols | Ethanol at 23°C | limited resistant, tests necessary to verify |
| Other | Ethyl Acetate at 23°C | limited resistant, tests necessary to verify |
| Other | Fuel; Diesel at 85°C | resistant |