Arnitel® EB501
- Chemical Family
- Polyesters
Arnitel® EB501 is a high-performance thermoplastic copolyester (TPC) known for its unique blend of flexibility, high-temperature resistance, strength, and outstanding processing characteristics. In industries like automotive and E&E, it is favored as a lighter, smarter, and more environmentally friendly alternative to traditional rubbers, leading to reduced environmental impact and lower system costs. This material is compatible with blow molding methods.
Product families
Applications
Automotive & Transportation — Automotive
- Chassis & Brake
- Powertrain & UTH
Product Families
Elastomers — Thermoplastic Elastomers
- Thermoplastic Polyester Elastomers (TPE-E)
Other characteristics
- Brand
- Arnitel
- Density
- 1180.0 - 1180.0 kg/m³
- Polymer Name
- Thermoplastic Copolyester Elastomer (TPC-ET)
- Strain at Break
- 50.0 - 50.0 %
- Processing Methods
- Blow Molding
- Markets
- Automotive & Transportation
- Technology
- Elastomers
- Packaging Type
- Bags
- Boxes
- Silos
- Super Sacks
- Quality Standards
- SAE J2558
- Certifications and Compliance
- ISO 14001
- OHSAS
- REACH (Europe)
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Blow Molding
Technical data
Table 1 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Strain at Break | >50 | % | ISO 527-1/-2 |
| Charpy Notched Impact Strength (at +23°C) | N | kJ/m² | ISO 179/1eA |
| Izod Notched Impact Strength (at +23°C) | N | kJ/m² | ISO 180/1A |
Table 2 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature (10°C/min) | 204 | °C | ISO 11357-1/-3 |
| Glass Transition Temperature (at 10°C/min) | -78 | °C | ISO 11357-1/-2 |
| Vicat Softening Temperature (50°C/h 50N) | 54 | °C | ISO 306 |
| Coefficient of Linear Thermal Expansion (parallel) | 2.2 | E-4/°C | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (normal) | 2.2 | E-4/°C | ISO 11359-1/-2 |
Table 3 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption in Water (at 23°C after 24h) | 0.88 | % | ISO 62 |
| Humidity Absorption | 1.19 | % | Sim. to ISO 62 |
| Density | 1180 | kg/m³ | ISO 1183 |
Table 4 of 6
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 140 | MPa | ISO 527-1/-2 |
| Stress at 5% strain | 6.5 | MPa | ISO 527-1/-2 |
| Stress at 10% strain | 11 | MPa | ISO 527-1/-2 |
| Stress at 50% strain | 18 | MPa | ISO 527-1/-2 |
| Stress at 100% strain | 21 | MPa | ISO 527-1/-2 |
| Stress at Break | 24 | MPa | ISO 527-1/-2 |
| Nominal Strain at Break | 150 | % | ISO 527-1/-2 |
| Compression Set Under Constant Strain (at 70°C) | 37 | % | ISO 815 |
| Tear Strength | 123 | kN/m | ISO 34-1; Method B |
| Shore A Hardness (3s) | 97 | — | ISO 868 |
| Shore A Hardness (15s) | 97 | — | ISO 868 |
| Shore D Hardness (3s) | 51 | — | ISO 868 |
Table 5 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Volume-Flow Rate (at 230 / * °C, 10 / * kg) | 7 | cm³/10min | ISO 1133 |
Химическая стойкость
24 rows| Characteristic | Value | Unit |
|---|---|---|
| Other | Acetic acid (10% by mass) at 23°C | resistant |
| Ketones | Acetone at 23°C | resistant |
| Other | Ammonium hydroxide (10% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | ASTM 1 at 23°C | resistant |
| Other | ASTM 3 at 23°C | resistant |
| Other | Brake fluids (DOT 3/4) at 23°C | not resistant |
| Other | Calcium chloride (10% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | Chloroform at 23°C | not resistant |
| Ethers | Diethyl ether at 23°C | limited resistant, tests necessary to verify |
| Alcohols | Ethanol at 23°C | limited resistant, tests necessary to verify |
| Other | Ethyl Acetate at 23°C | limited resistant, tests necessary to verify |
| Other | Fuel; Diesel at 85°C | resistant |