Arnitel® CM600-V
- Chemical Family
- Polyesters
Arnitel® CM600-V, a high-performance ThermoPlastic Copolyester (TPC) renowned for its exceptional blend of flexibility, high-temperature resistance, strength, and superior processing capabilities. In automotive and E&E industries, it serves as a lighter, more intelligent, and environmentally friendly replacement for conventional rubber. Crafted through extrusion and injection molding, it also boasts halogen-free flame-retardant properties.
Product families
Applications
- Electrical & Electronic Systems
- Automotive Electronics
- Jacketing & Insulation
Product Families
- Thermoplastic Polyester Elastomers (TPE-E)
Other characteristics
- Brand
- Arnitel
- Density
- 1320.0 - 1320.0 kg/m³
- End Uses
- Cables, Wires
- Polymer Name
- Thermoplastic Copolyester Elastomer (TPC-ET)
- Strain at Break
- 50.0 - 50.0 %
- Processing Methods
- Extrusion, Injection Molding
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Technology
- Elastomers
- Packaging Type
- Bags
- Boxes
- Silos
- Super Sacks
- Labeling Claims
- Halogen-free
- Quality Standards
- UL Yellow Card (E47960)
- Material Features
- Flame Retardant
- High Thermo-Oxidative Stability
- Certifications and Compliance
- ISO 14001
- OHSAS
- REACH (Europe)
- Plastics and Elastomers End Uses
- Cables
- Wires
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Injection Molding
- Wire and Cable Insulation Application Data
Arnitel® TPC allows for reliable solutions due its high temperature resistance (class T3 and T4, Class D (150°C) enabling thin and ultra thin wall designs, Class E (175°C) >20 mm2 thick and thin wall); Arnitel® TPC allows for cost effective solutions (up to 50% lower system costs versus ETFE/FEP, 40% weight down versus XL PO at similar costs); Arnitel® TPC allows for sustainable solutions due to availability of halogen free flameretardant grades
Technical data
Table 1 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Yield Stress | 21 | MPa | ISO 527-1/-2 |
| Yield Strain | 18 | % | ISO 527-1/-2 |
| Nominal Strain at Break | >50 | % | ISO 527-1/-2 |
| Charpy Notched Impact Strength (at +23°C) | 11 | kJ/m² | ISO 179/1eA |
| Charpy Notched Impact Strength (at -30°C) | 3 | kJ/m² | ISO 179/1eA |
| Izod Notched Impact Strength (at +23°C) | 11 | kJ/m² | ISO 180/1A |
| Izod Notched Impact Strength (at -20°C) | 3.2 | kJ/m² | ISO 180/1A |
Table 2 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature (10°C/min) | 205 | °C | ISO 11357-1/-3 |
| Glass Transition Temperature (at 10°C/min) | -10 | °C | ISO 11357-1/-2 |
| Vicat Softening Temperature (50°C/h 50N) | 85 | °C | ISO 306 |
Table 3 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Relative Permittivity (100Hz) | 4.2 | — | IEC 62631-2-1 |
| Relative Permittivity (1 MHz) | 3.7 | — | IEC 62631-2-1 |
| Dissipation Factor (100 Hz) | 157 | E-4 | IEC 62631-2-1 |
| Dissipation Factor (1 MHz) | 385 | E-4 | IEC 62631-2-1 |
| Volume Resistivity | >1E13 | Ohm*m | IEC 62631-3-1 |
| Electric Strength | 18.7 | kV/mm | IEC 60243-1 |
Table 4 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption in Water (at 23°C after 24h) | 0.18 | % | ISO 62 |
| Humidity Absorption | 0.1 | % | Sim. to ISO 62 |
| Density | 1320 | kg/m³ | ISO 1183 |
Table 5 of 7
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 540 | MPa | ISO 527-1/-2 |
| Stress at 5% strain | 17 | MPa | ISO 527-1/-2 |
| Stress at 10% strain | 21 | MPa | ISO 527-1/-2 |
| Stress at 50% strain | 20 | MPa | ISO 527-1/-2 |
| Stress at 100% strain | 18 | MPa | ISO 527-1/-2 |
| Stress at Break | 20.5 | MPa | ISO 527-1/-2 |
| Nominal Strain at Break | 250 | % | ISO 527-1/-2 |
| Compression Set Under Constant Strain (at 70°C) | 50 | % | ISO 815 |
| Tear Strength | 132 | kN/m | ISO 34-1; Method B |
| Shore A Hardness (3s) | 99 | — | ISO 868 |
| Shore A Hardness (15s) | 98 | — | ISO 868 |
| Shore D Hardness (3s) | 62 | — | ISO 868 |
Table 6 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Volume-Flow Rate (at 230 / * °C, 2.16 / * kg) | 13 | cm³/10min | ISO 1133 |
Химическая стойкость
24 rows| Characteristic | Value | Unit |
|---|---|---|
| Other | Acetic acid (10% by mass) at 23°C | resistant |
| Ketones | Acetone at 23°C | resistant |
| Other | Ammonium hydroxide (10% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | ASTM 1 at 23°C | resistant |
| Other | ASTM 3 at 23°C | resistant |
| Other | Brake fluids (DOT 3/4) at 23°C | not resistant |
| Other | Calcium chloride (10% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | Chloroform at 23°C | not resistant |
| Ethers | Diethyl ether at 23°C | limited resistant, tests necessary to verify |
| Alcohols | Ethanol at 23°C | limited resistant, tests necessary to verify |
| Other | Ethyl Acetate at 23°C | limited resistant, tests necessary to verify |
| Other | Fuel; Diesel at 85°C | resistant |