Akulon® Diablo HT-HG6
- Chemical Family
- Polyamides
Akulon® Diablo HT-HG6 is a polyamide 6/66 (PA 6/66) that functions as a resin and is characterized by its heat stabilization, high thermo-oxidative stability, and lightweight properties. It is predominantly used in the automotive and transportation markets, particularly in applications related to cooling and climate systems, exterior and body components, as well as interior elements.
Product families
Automotive & Transportation — Automotive
- Cooling & Climate
- Exterior & Body
- Interior
Other characteristics
- Brand
- Akulon®
- Polymer Name
- Polyamide 6/66 (PA 6/66)
- Fillers Included
- Glass Fiber
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding, Injection Molding
- Reinforcement Material
- Glass Fibers
- Markets
- Automotive & Transportation
- Technology
- Composite Materials
- Plastics
- OEM Standards
- General Motors
- PSA
- Packaging Type
- Bags
- Boxes
- Silos
- Super Sacks
- Material Features
- Heat Stabilized
- High Thermo-Oxidative Stability
- Light Weight
- OEM Specifications
- GM GMW15702-022331-PA66-PA6 GF 30
- PSA Peugeot-Citroen FTM 64 0039
- Reinforcement Form
- Tape
- Unidirectional Fabric
- Certifications and Compliance
- ISO 14001
- OHSAS
- REACH (Europe)
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Injection Molding
- Plastics and Elastomers End Uses
- Air Ducts
- Air Intake Manifolds
- Cooler Caps
- Door Panel
- Flooring
- Valves
- Wheel Housing Parts
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 4
43 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 9800 / 5500 | MPa | ISO 527-1/-2 |
| Tensile Modulus (-40°C) | 10000 / - | MPa | ISO 527-1/-2 |
| Tensile Modulus (40°C) | 9300 / - | MPa | ISO 527-1/-2 |
| Tensile Modulus (120°C) | 4250 / - | MPa | ISO 527-1/-2 |
| Tensile Modulus (150°C) | 3900 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (160°C) | 3300 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (180°C) | 2950 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (200°C) | 2600 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (210°C) | 2440 / * | MPa | ISO 527-1/-2 |
| Stress at Break | 190 / 95 | MPa | ISO 527-1/-2 |
| Stress at Break (-40°C) | 250 / - | MPa | ISO 527-1/-2 |
| Stress at Break (100°C) | 97 / - | MPa | ISO 527-1/-2 |
Table 2 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature (10°C/min) | 260 / * | °C | ISO 11357-1/-3 |
| Temperature of Deflection Under Load (1.80 MPa) | 235 / * | °C | ISO 75-1/-2 |
| Temperature of Deflection Under Load (0.45 MPa) | 255 / * | °C | ISO 75-1/-2 |
Table 3 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption | 6.9 / * | % | Sim. to ISO 62 |
| Water Absorption in Water (at 23°C after 24h) | 3 / * | % | ISO 62 |
| Humidity Absorption | 2.4 / * | % | Sim. to ISO 62 |
| Density | 1370 / - | kg/m³ | ISO 1183 |
Table 4 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Molding Shrinkage (parallel) | 0.3 / * | % | ISO 294-4 |
| Molding Shrinkage (normal) | 1.1 / * | % | ISO 294-4 |