To catalogue
Xytron™ G4012T
- Chemical Family
- Polyphenylene Sulfide (PPS)
Xytron™ G4012T is a high-performance plastic compound from Envalior that is based on PPS (polyphenylene sulfide). It offers extremely good chemical resistance, dimensional stability, intrinsic flame retardancy, and high stiffness. Because of its outstanding properties, it contributes to excellent performance in many different applications. A suitable processing technology for the product is injection molding.
Product families
Plastics — Engineering & Specialty Polymers
- High Performance Thermoplastics
Other characteristics
- Brand
- Xytron
- Polymer Name
- Polyphenylene Sulfide (PPS)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 14500.0 - 14500.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Packaging Type
- Bags
- Boxes
- Silos
- Super Sacks
- Labeling Claims
- Halogen-free
- Quality Standards
- UL Yellow Card (E467723)
- Material Features
- Chemical Resistant
- Heat Resistance
- UL Flame Rated
- Certifications and Compliance
- ISO 14001
- OHSAS
- REACH (Europe)
- UL 94
- Plastics and Elastomers End Uses
- Automotive E-Motor Bobbins
- Coil Insulation
- Mini Projectors
- Plastics and Elastomers Functions
- Resin
- Coil Insulation Application Data
Stanyl® PA46 allows for reliable solutions due to a high temperature resistance (UL1446 class H certified) and creep resistance at elevated temperatures, high toughness levels and good electrical insulation properties; Stanyl® PA46 allows for cost effective solutions due to a good flowability and processability enabling therefore thin wall designs; Xytron™ PPS allows for super high temperatrue resistance for long term.
Technical data
Table 1 of 6
33 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 15000 | MPa | ISO 527-1/-2 |
| Tensile Modulus (-40°C) | 16000 | MPa | ISO 527-1/-2 |
| Tensile Modulus (120°C) | 7300 | MPa | ISO 527-1/-2 |
| Tensile Modulus (160°C) | 5200 | MPa | ISO 527-1/-2 |
| Tensile Modulus (200°C) | 3400 | MPa | ISO 527-1/-2 |
| Stress at Break | 200 | MPa | ISO 527-1/-2 |
| Stress at Break (-40°C) | 235 | MPa | ISO 527-1/-2 |
| Stress at Break (120°C) | 105 | MPa | ISO 527-1/-2 |
| Stress at Break (160°C) | 73 | MPa | ISO 527-1/-2 |
| Stress at Break (200°C) | 55 | MPa | ISO 527-1/-2 |
| Strain at Break | 2 | % | ISO 527-1/-2 |
| Strain at Break (at -40°C) | 2 | % | ISO 527-1/-2 |
Table 2 of 6
17 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature (10°C/min) | 280 | °C | ISO 11357-1/-3 |
| Glass Transition Temperature (at 10°C/min) | 90 | °C | ISO 11357-1/-2 |
| Temperature of Deflection Under Load (1.80 MPa) | 265 | °C | ISO 75-1/-2 |
| Temperature of Deflection Under Load (0.45 MPa) | 280 | °C | ISO 75-1/-2 |
| Temperature of Deflection Under Load (8.00 MPa) | 185 | °C | ISO 75-1/-2 |
| Coefficient of Linear Thermal Expansion (parallel) | 0.16 | E-4/°C | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (normal) | 0.4 | E-4/°C | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (parallel, above Tg) | 0.13 | E-4/°C | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (normal, above Tg) | 0.85 | E-4/°C | ISO 11359-1/-2 |
| Burning Behaviour (at 1.5 mm Nominal Thickness) | UL V-0 | class | IEC 60695-11-10 |
| Burning Behaviour (at 3.0 mm Nominal Thickness) | UL V-0 | class | IEC 60695-11-10 |
| Relative Temperature Index (Electrical, 0.8 mm) | 130 | °C | UL746B |
Table 3 of 6
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Relative Permittivity (1GHz) | 4 | — | IEC 60250 |
| Relative Permittivity (5GHz) | 4 | — | IEC 60250 |
| Dissipation Factor (1GHz) | 35 | E-4 | IEC 60250 |
| Dissipation Factor (5GHz) | 55 | E-4 | IEC 60250 |
| Volume Resistivity | >1E13 | Ohm*m | IEC 62631-3-1 |
| Surface Resistivity | >1E15 | Ohm | IEC 62631-3-2 |
| Electric Strength | 32 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Dielectric Strength | 31 | kV/mm | IEC 60234 |
Table 4 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption in Water (at 23°C after 24h) | 0.04 | % | ISO 62 |
| Humidity Absorption | 0.04 | % | Sim. to ISO 62 |
| Density | 1650 | kg/m³ | ISO 1183 |
Table 5 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Molding Shrinkage (parallel) | 0.2 | % | ISO 294-4 |
| Molding Shrinkage (normal) | 0.5 | % | ISO 294-4 |
Химическая стойкость
415 rows| Characteristic | Value | Unit |
|---|---|---|
| Other | 1% nonylphenoxy-polyethyleneoxy ethanol in water at 23°C | resistant |
| Other | 50% Oleic acid + 50% Olive Oil at 23°C | resistant |
| Other | Acetaldehyde (40% by mass) at 23°C | resistant |
| Other | Acetamide (50% by mass) at 23°C | resistant |
| Other | Acetamide (50% by mass) at >140°C | resistant |
| Other | Acetic acid (10% by mass) at 100°C | resistant |
| Other | Acetic acid (10% by mass) at 23°C | resistant |
| Acids | Acetic Acid (5% by mass) at 23°C | resistant |
| Other | Acetic acid (95% by mass) at 23°C | resistant |
| Ketones | Acetone at 23°C | resistant |
| Other | Acetophenone at 23°C | resistant |
| Other | Acetyl chloride at 23°C | resistant |