Akulon® Ultraflow SG-FHGS3
- Chemical Family
- Polyamides
Akulon® Ultraflow SG-FHGS3 is a high-performance polyamide 6 and polyamide 66 material trusted globally for applications spanning automotive, electronics, electrical, furniture, and packaging. In molded parts, it provides an impressive combination of design simplicity and processing ease, accompanied by exceptional mechanical properties across a wide temperature range and diverse conditions. For extrusion, it sets industry standards, featuring remarkable strength, resilience, and ease of processing. Injection molding is the preferred processing technology for this product, which offers notable attributes, including 15% glass reinforcement, halogen-free, and red-phosphorous-free properties.
Product families
Automotive & Transportation — Automotive
- Exterior & Body
- Interior
Other characteristics
- Brand
- Akulon®
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber
- Processing Methods
- Injection Molding, Injection Molding
- Reinforcement Material
- Glass Fibers
- Markets
- Automotive & Transportation
- Technology
- Composite Materials
- Plastics
- OEM Standards
- General Motors
- Packaging Type
- Bags
- Boxes
- Silos
- Super Sacks
- Labeling Claims
- Halogen-free
- Phosphorus-free
- Material Features
- Light Weight
- OEM Specifications
- GM GMW16864P-PA6 GF 15H
- Reinforcement Form
- Tape
- Unidirectional Fabric
- Certifications and Compliance
- ISO 14001
- OHSAS
- REACH (Europe)
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Injection Molding
- Plastics and Elastomers End Uses
- Door Panel
- Flooring
- Wheel Housing Parts
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 4
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 6850 / 4450 | MPa | ISO 527-1/-2 |
| Tensile Modulus (-40°C) | 6400 / - | MPa | ISO 527-1/-2 |
| Tensile Modulus (120°C) | 2800 / - | MPa | ISO 527-1/-2 |
| Tensile Modulus (150°C) | 2250 / * | MPa | ISO 527-1/-2 |
| Stress at Break | 110 / 70 | MPa | ISO 527-1/-2 |
| Stress at Break (-40°C) | 140 / - | MPa | ISO 527-1/-2 |
| Stress at Break (120°C) | 54 / - | MPa | ISO 527-1/-2 |
| Stress at Break (150°C) | 46 / * | MPa | ISO 527-1/-2 |
| Strain at Break | 3.1 / 5.3 | % | ISO 527-1/-2 |
| Strain at Break (at -40°C) | 3.6 / - | % | ISO 527-1/-2 |
| Strain at Break (at 120°C) | 8.5 / - | % | ISO 527-1/-2 |
| Strain at Break (at 150°C) | 9.5 / * | % | ISO 527-1/-2 |
Table 2 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature (10°C/min) | 260 / * | °C | ISO 11357-1/-3 |
| Temperature of Deflection Under Load (1.80 MPa) | 230 / * | °C | ISO 75-1/-2 |
| Burning Behaviour (at 1.5 mm Nominal Thickness) | V-0 / * | class | IEC 60695-11-10 |
| Burning Behaviour (at 0.75 mm Nominal Thickness) | V-0 / * | class | IEC 60695-11-10 |
Table 3 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1300 / - | kg/m³ | ISO 1183 |
Химическая стойкость
384 rows| Characteristic | Value | Unit |
|---|---|---|
| Other | Acetaldehyde (40% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | Acetamide (50% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | Acetamide (50% by mass) at >140°C | not resistant |
| Other | Acetic acid (10% by mass) at 100°C | not resistant |
| Other | Acetic acid (10% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | Acetic acid (95% by mass) at 23°C | not resistant |
| Ketones | Acetone at 23°C | resistant |
| Other | Acetophenone at 23°C | resistant |
| Other | Acetyl chloride at 23°C | not resistant |
| Other | Acetylene at 23°C | resistant |
| Other | Acrylic acid at 23°C | not resistant |
| Other | Aliphatic amines at 23°C | resistant |