Akulon® S223-HG7
- Chemical Family
- Polyamides
Akulon® S223-HG7 is a high-performance material that blends the characteristics of polyamide 6 and polyamide 66. It is widely used by customers worldwide in various applications, including automotive, electronics, electrical, furniture, and packaging. When employed in molded parts, this material excels in providing an excellent balance between ease of design and processing while delivering outstanding mechanical properties over a wide temperature range and under diverse conditions.
Other characteristics
- Brand
- Akulon®
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding, Injection Molding
- Reinforcement Material
- Glass Fibers
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Flame Rating
- UL 94 HB
- Technology
- Composite Materials
- Plastics
- OEM Standards
- General Motors
- Mercedes
- PSA
- Renault
- Packaging Type
- Bags
- Boxes
- Silos
- Super Sacks
- Quality Standards
- UL Yellow Card (E43392)
- UL Yellow Card (E47960)
- Material Features
- Light Weight
- UL Flame Rated
- OEM Specifications
- GM GMW3038P-PA66 GF 35J
- GM GMW3038P-PA66 GF35H
- MERCEDES DBL 5405.01
- PSA Peugeot-Citroen 01994-16-00820
- RENAULT PMR
- Reinforcement Form
- Tape
- Unidirectional Fabric
- Application Data
Akulon® PA6, Arnite® PBT and Stanyl® PA46 allow for reliable solutions due to their high temperature resistance (much higher than PP) and due to their good electrical insulation properties. Akulon® PA6, Arnite® PBT and Stanyl® PA46 allow for cost effective solutions due to their ease of processability
- Certifications and Compliance
- ISO 14001
- OHSAS
- REACH (Europe)
- UL 94
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Injection Molding
- Fuse Holders Application Data
Akulon® PA6, Arnite® PBT and Stanyl® PA46 allow for reliable solutions due to their high temperature resistance (much higher than PP) and due to their good electrical insulation properties. Akulon® PA6, Arnite® PBT and Stanyl® PA46 allow for cost effective solutions due to their ease of processability
- Plastics and Elastomers End Uses
- Air Intake Manifolds
- Automotive Electronics
- Connectors
- Cooler Caps
- Door Panel
- E-Boxes
- Flooring
- Fuse Holders
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 6
38 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 11500 / 7550 | MPa | ISO 527-1/-2 |
| Tensile Modulus (-40°C) | 12000 / - | MPa | ISO 527-1/-2 |
| Tensile Modulus (100°C) | 5700 / - | MPa | ISO 527-1/-2 |
| Tensile Modulus (120°C) | 5350 / - | MPa | ISO 527-1/-2 |
| Tensile Modulus (140°C) | 5000 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (150°C) | 4800 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (160°C) | 4600 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (180°C) | 4200 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (200°C) | 3850 / * | MPa | ISO 527-1/-2 |
| Stress at Break | 210 / 140 | MPa | ISO 527-1/-2 |
| Stress at Break (-40°C) | 270 / - | MPa | ISO 527-1/-2 |
| Stress at Break (100°C) | 120 / - | MPa | ISO 527-1/-2 |
Table 2 of 6
18 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature (10°C/min) | 260 / * | °C | ISO 11357-1/-3 |
| Temperature of Deflection Under Load (1.80 MPa) | 247 / * | °C | ISO 75-1/-2 |
| Temperature of Deflection Under Load (0.45 MPa) | 260 / * | °C | ISO 75-1/-2 |
| Coefficient of Linear Thermal Expansion (parallel) | 0.2 / * | E-4/°C | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (normal) | 0.6 / * | E-4/°C | ISO 11359-1/-2 |
| Burning Behaviour (at 1.5 mm Nominal Thickness) | UL HB / * | class | IEC 60695-11-10 |
| Burning Behaviour (at 3.0 mm Nominal Thickness) | UL HB / * | class | IEC 60695-11-10 |
| Burning Behaviour (at 0.75 mm Nominal Thickness) | HB / * | class | IEC 60695-11-10 |
| Relative Temperature Index (Electrical, 0.71 / * mm) | 140 / * | °C | UL746B |
| Relative Temperature Index (Electrical, 3 / * mm) | 140 / * | °C | UL746B |
| Relative Temperature Index (with impact, 0.71 / * mm) | 120 / * | °C | UL746B |
| Relative Temperature Index (with impact, 3 / * mm) | 130 / * | °C | UL746B |
Table 3 of 6
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Relative Permittivity (100Hz) | 4 / 10 | — | IEC 62631-2-1 |
| Relative Permittivity (1 MHz) | 3.6 / 4 | — | IEC 62631-2-1 |
| Dissipation Factor (100 Hz) | 50 / 3000 | E-4 | IEC 62631-2-1 |
| Dissipation Factor (1 MHz) | 140 / 1000 | E-4 | IEC 62631-2-1 |
| Volume Resistivity | 1E12 / 1E10 | Ohm*m | IEC 62631-3-1 |
| Surface Resistivity | - / 1E13 | Ohm | IEC 62631-3-2 |
| Electric Strength | 35 / 30 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 500 / 500 | V | IEC 60112 |
Table 4 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption | 5.5 / * | % | Sim. to ISO 62 |
| Humidity Absorption | 1.5 / * | % | Sim. to ISO 62 |
| Density | 1410 / - | kg/m³ | ISO 1183 |
Table 5 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Volume-Flow Rate (at 275 / * °C, 5 / * kg) | 10.6 / * | cm³/10min | ISO 1133 |
| Melt Flow Index (at 275 / * °C, 5 / * kg) | 13.3 / * | g/10min | ISO 1133 |
| Molding Shrinkage (parallel) | 0.2 / * | % | Sim. to ISO 294-4 |
| Molding Shrinkage (normal) | 1 / * | % | Sim. to ISO 294-4 |
Химическая стойкость
384 rows| Characteristic | Value | Unit |
|---|---|---|
| Other | Acetaldehyde (40% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | Acetamide (50% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | Acetamide (50% by mass) at >140°C | not resistant |
| Other | Acetic acid (10% by mass) at 100°C | not resistant |
| Other | Acetic acid (10% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | Acetic acid (95% by mass) at 23°C | not resistant |
| Ketones | Acetone at 23°C | resistant |
| Other | Acetophenone at 23°C | resistant |
| Other | Acetyl chloride at 23°C | not resistant |
| Other | Acetylene at 23°C | resistant |
| Other | Acrylic acid at 23°C | not resistant |
| Other | Aliphatic amines at 23°C | resistant |