Akulon® Diablo HT-HG0
- Chemical Family
- Polyamides
Akulon® Diablo HT-HG0 is a polyamide 6/66 (PA 6/66) resin known for its heat stabilization, high stiffness, high strength, high thermo-oxidative stability, and lightweight characteristics. It is primarily employed in the automotive and transportation markets for a wide range of applications.
Product families
Automotive & Transportation — Automotive
- Cooling & Climate
- Exterior & Body
- Interior
Other characteristics
- Brand
- Akulon®
- Polymer Name
- Polyamide 6/66 (PA 6/66)
- Fillers Included
- Glass Fiber
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding, Injection Molding
- Reinforcement Material
- Glass Fibers
- Safety
For the safety properties of the material, we refer to our SDS which can be ordered at our sales offices. During practical operation we advise to wear personal safety protections for hand/eye/body.
- Markets
- Automotive & Transportation
- PACKAGING
Akulon® grades are supplied in airtight, moisture- proof packaging.
- Technology
- Composite Materials
- Plastics
- OEM Standards
- Callout
- Renault
- Packaging Type
- Bags
- Boxes
- Silos
- Super Sacks
- Material Features
- Heat Stabilized
- High Stiffness
- High Strength
- High Thermo-Oxidative Stability
- Light Weight
- OEM Specifications
- CALLOUT ASTM D6779 PA0820A64490 (9=245)
- RENAULT PMR
- Reinforcement Form
- Tape
- Unidirectional Fabric
- Certifications and Compliance
- ISO 14001
- OHSAS
- REACH (Europe)
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Injection Molding
- Plastics and Elastomers End Uses
- Air Intake Manifolds
- Cooler Caps
- Door Panel
- Flooring
- Valves
- Wheel Housing Parts
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 4
41 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 16500 / 10000 | MPa | ISO 527-1/-2 |
| Tensile Modulus (-40°C) | 17000 / - | MPa | ISO 527-1/-2 |
| Tensile Modulus (40°C) | 15000 / - | MPa | ISO 527-1/-2 |
| Tensile Modulus (100°C) | 7100 / - | MPa | ISO 527-1/-2 |
| Tensile Modulus (120°C) | 6700 / - | MPa | ISO 527-1/-2 |
| Tensile Modulus (150°C) | 5600 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (180°C) | 4650 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (200°C) | 4100 / * | MPa | ISO 527-1/-2 |
| Stress at Break | 235 / 145 | MPa | ISO 527-1/-2 |
| Stress at Break (-40°C) | 300 / - | MPa | ISO 527-1/-2 |
| Stress at Break (100°C) | 120 / - | MPa | ISO 527-1/-2 |
| Stress at Break (120°C) | 105 / - | MPa | ISO 527-1/-2 |
Table 2 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature (10°C/min) | 260 / * | °C | ISO 11357-1/-3 |
| Temperature of Deflection Under Load (1.80 MPa) | 245 / * | °C | ISO 75-1/-2 |
| Temperature of Deflection Under Load (0.45 MPa) | 255 / * | °C | ISO 75-1/-2 |
Table 3 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption | 4.8 / * | % | Sim. to ISO 62 |
| Water Absorption in Water (at 23°C after 24h) | 1.8 / * | % | ISO 62 |
| Humidity Absorption | 1.7 / * | % | Sim. to ISO 62 |
| Density | 1580 / - | kg/m³ | ISO 1183 |
Table 4 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Molding Shrinkage (parallel) | 0.3 / * | % | ISO 294-4 |
| Molding Shrinkage (normal) | 1 / * | % | ISO 294-4 |