G&E Blended Butyl

G&E Blended Butyl is produced by carefully combining selected feedstocks for uniform viscosity and rheology. G&E Blended Butyl is excellent for cost reduction in all types of Butyl applications when blended with prime butyl rubber.

Properties

Physical Form: Solid

Product families

Applications

Adhesives & Sealants — Other Adhesives & Sealants Applications; Consumer Goods — Sports & Recreation

Automotive & Transportation — Automotive

Other Automotive Applications

Industrial — Chemical & Industrial Manufacturing

Other Industrial Applications

Product Families

Elastomers — Thermoplastic Elastomers

Elastomer Blends

Other characteristics

Brand: G&E
Polymer Name: Butyl Rubber (IIR)
Markets: Adhesives & Sealants
Automotive & Transportation
Consumer Goods
Industrial
PACKAGING: Thirty-six, 75 lb. (34 kg.) bales wrapped in low-melt polyethylene film are packaged in Returnable Metal Boxes weighing 2,700 lbs (1.23 MT) each. Corrugated Boxes are available with a weight of 2200 lbs (1 MT)
Technology: Elastomers
Packaging Type: Bales
Boxes

Technical data

Table 1 of 1

15 rows

Characteristic	Value	Unit	Method
MOONEY VISCOSITY ML 1+8 at125°C (257°F)	40 ± 10	—	ASTM D 1646
MOONEY VISCOSITY Raw Polymer specific Gravity	0.92	—	ASTM F 970
MOONEY VISCOSITY (% Ash Content)	Max. 2	wt%	ASTM D 5667-95
MOONEY VISCOSITY (Volatile Matter)	Max. 1	wt%	ASTM D 5668
ODR RHEOMETER ML (30 Minutes/3° Arc at 177°C (350°F))	2.0 Typical	—	ASTM D 2084 Ts2
ODR RHEOMETER MH (30 Minutes/3° Arc at 177°C (350°F))	4.0 Typical	—	ASTM D 2084 Tc90
Tensile (Cured 40 Min at 150°C(302°F))	2400	psi	ASTM D 412
Elongation (Cured 40 Min at 150°C(302°F))	575	%	ASTM D 412
300 % Modulus (Cured 40 Min at 150°C(302°F))	1200	psi	ASTM D 412
G&E Blended IIR (Internal Mixer Method)	100	pts.	ASTM D 3188-06 (2010)
Zinc Oxide (Internal Mixer Method)	3	pts.	ASTM D 3188-06 (2010)
Sulfur (Internal Mixer Method)	1.75	pts.	ASTM D 3188-06 (2010)