G&E 9007
G&E 9007 BMB is mechanically mixed SBR Black masterbatch. This material can be used to replace similar co-precipitated masterbatch in most applications. G&E 9007 contains 100 parts SBR, 52 parts of N-234 series carbon black, and 10 parts Highly Napthenic Oil.
Properties
- Physical Form
- Masterbatch
- Solid
Other characteristics
- Brand
- G&E
- Color
- Black
- Functions
- Pigment
- Pigment Type
- Inorganic Pigments
- Carrier
- Resin-based
- Styrene Butadiene Rubber (SBR)
- Markets
- Industrial
- PACKAGING
Standard Package: Approximately 30"x38"x3/8" slabs on a 4 -way entry heat treated wood pallet; approximately 2,200 lbs. net (1 Metric Ton)..
- Applications
- Industrial — Other Industrial Applications
- Technology
- Pigments & Colorants
- Plastics
- Plastics and Elastomers Functions
- Pigment
Technical data
Table 1 of 1
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UNMILLED MOONEY VISCOSITY (UMS 4+4 at100°C) | 55-85 | — | ASTM D 1646 |
| ODR RHEOMETER ML (12 Minutes/3° Arc at 177°C) | 10.5 | — | ASTM D 2084 |
| ODR RHEOMETER MH (12 Minutes/3° Arc at 177°C) | 66 | — | ASTM D 2084 |
| ODR RHEOMETER Ts2 (12 Minutes/3° Arc at 177°C) | 2.2 | — | ASTM D 2084 |
| ODR RHEOMETER Tc90 (12 Minutes/3° Arc at 177°C) | 7 | — | ASTM D 2084 |
| Tensile (Cured 35 Min at 145°C) | min. 2550 | psi | ASTM D 412 |
| Elongation (Cured 35 Min at 145°C) | min. 365 | % | ASTM D 412 |
| 300 % Modulus (Cured 35 Min at 145°C) | min. 1150 | psi | ASTM D 412 |
| Specific Gravity (Cured 35 Min at 145°C) | 1.12 | — | ASTM D 412 |
| 1605 BMB (Mill Mixed) | 162 | pts. | ASTM D 3186 |
| Zinc Oxide (Mill Mixed) | 3 | pts. | ASTM D 3186 |
| Stearic Acid (Mill Mixed) | 1.5 | pts. | ASTM D 3186 |