G&E Blended Chlorobutyl
- Chemical Family
- Chlorinated CompoundsHalogenated Compounds
G&E Blended Chlorobutyl is produced by carefully combining selected feedstocks for uniform viscosity and rheology. G&E Blended Chlorobutyl is excellent for cost reduction in applications such as innerliners and most mechanical goods when blended with prime Chlorobutyl.
Properties
- Physical Form
- Solid
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Other Industrial Applications
Product Families
Elastomers — Specialty Elastomers
- Butyl Rubbers
Other characteristics
- Brand
- G&E
- Polymer Name
- Chlorobutyl Rubber
- Markets
- Industrial
- PACKAGING
Thirty-six, 75 lb. (34 kg.) bales wrapped in low-melt polyethylene film are packaged in Returnable Metal Boxes weighing 2,700 lbs (1.23 MT) each.
- Technology
- Elastomers
- Packaging Type
- Bales
- Boxes
Technical data
Table 1 of 1
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| MOONEY VISCOSITY ML 1+8 at125°C (257°F) | 35 ± 10 | — | ASTM D 1646 |
| MOONEY VISCOSITY Raw Polymer specific Gravity | 0.93 | — | ASTM F 970 |
| MOONEY VISCOSITY (XRF Bromine Content) | 1.40-2.60 | % | (G&E Method) |
| MOONEY VISCOSITY ( % Ash Content) | Max. 2 | wt% | ASTM D 5667 -95 |
| MOONEY VISCOSITY (Volatile Matter, % weight) | Max. 1 | wt% | ASTM D 5668 |
| ODR RHEOMETER ML (30 Minutes/3° Arc at 177°C (350°F)) (14 lbr) | 2 | mins | ASTM D 2084 Ts2 |
| ODR RHEOMETER MH (30 Minutes/3° Arc at 177°C (350°F)) (37 lbr) | 9 | mins | ASTM D 2084 Tc90 |
| Tensile (Cured 40 Min at 150°C(302°F)) | 1500 min | — | ASTM D 412 |
| Elongation (Cured 40 Min at 150°C(302°F)) | 375 min | — | ASTM D 412 |
| 300 % Modulus (Cured 40 Min at 150°C(302°F)) | 800 min | — | ASTM D 412 |
| G&E Blended IIR (Internal Mixer Method) | 100 | — | ASTM D 3958-06 |
| Zinc Oxide (Internal Mixer Method) | 5 | — | ASTM D 3958-06 |