To catalogue
TPE Solutions TPE 40D COPE BK UV
- Chemical Family
- Polyesters
TPE Solutions TPE 40D COPE BK UV is a Copolyester Elastomer (COPE) polymer.
Product families
Elastomers — Thermoplastic Elastomers
- Thermoplastic Polyester Elastomers (TPE-E)
Other characteristics
- Polymer Name
- Copolyester Elastomer (COPE)
- Strain at Break
- 650.0 - 650.0 %
- Flexural Modulus
- 46.0 - 46.0 MPa
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Applications
Automotive & Transportation — Other Automotive & Transportation Applications; Building & Construction — Other Building & Construction Applications; Consumer Goods — Other Consumer Goods Applications; Electrical & Electronics — Other Electrical & Electronics Applications
- Technology
- Elastomers
Technical data
Table 1 of 5
29 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Bayshore Resilience | 58 | % | Internal |
| Tensile modulus (1mm/min) | 55 | MPa | ISO 527-2/1A |
| Tensile strain at break (50mm/min) | 650 | % | ISO 527-2/1A |
| Flexural Modulus (-40°C) | 270 | MPa | ISO 178 |
| Flexural Modulus (100°C) | 26 | MPa | ISO 178 |
| Flexural Modulus (23°C) | 46 | MPa | ISO 178 |
| Hardness (15 sec) | 40 | Shore D | ISO 868 |
| Hardness (15 sec) | 92 | Shore D | ISO 868 |
| Izod Notched Impact Strength (-30°C) | NB | kJ/m² | ISO 180/1A |
| Izod Notched Impact Strength (-40°C) | NB | kJ/m² | ISO 180/1A |
| Izod Notched Impact Strength (23°C) | NB | kJ/m² | ISO 180/1A |
| Izod Unnotched Impact Strength (23°C) | NB | kJ/m² | ISO 180/10 |
Table 2 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1110 | kg/m³ | ISO 1183 |
| Melt Flow Rate | 13.3 | g/10 | ISO 1133 |
| MFR Test Load | 2.16 | kg | ISO 1133 |
| MFR Test Temperature | 220 | °C | ISO 1133 |
| Mold shrinkage (Parallel) | 1.3 | % | ISO 294-4 |
Table 3 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting temperature (10°C/min) | 192 | °C | ISO 11357-1,-2,-3 |
| Flammability (Thickness H) | HB | class | UL94 |
| Thickness tested (H) | 1.5 | mm | UL94 |
| DTUL (0.45 MPa) | 47 | °C | ISO 75-1/-2 |
Table 4 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption (23°C-sat) | 0.5 | % | ISO 62 |
Table 5 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Comparative Tracking Index | min. 600 | — | IEC 60112 |
| Electric Strength | 26 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 4.9 | — | IEC 60250 |
| Surface Resistivity | 200000000000000 | Ohm | IEC 60093 |
| Volume Resistivity | 20000000000 | Ohm*m | IEC 60093 |
| Comparative tracking index CTI | min. 600 | — | IEC 60112 |