2MILA PE2NT76 - 17
- Chemical Family
- PolyethylenesPolyolefins
2MILA PE2NT76 - 17 is intended for further processing by extrusion blow molding method into domestic and industrial-use articles with a capacity of up to 3 liters such as flasks, water bottles, bottles for household chemistry and cosmetics.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
- Food & Beverage Packaging
- Non-Food Consumer Packaging
Product Families
- Polyolefins
Other characteristics
- Polymer Name
- High Density Polyethylene (HDPE)
- Melt Flow Index
- 2.3 - 3.3 g/10 min
- Processing Methods
Blow Molding, Blown Film Extrusion, Extrusion, Film Extrusion
- Markets
- Printing & Packaging
- Storage
Polyethylene shall be stored in enclosed dry space preventing from direct sunlight on shelves or pallets at least 5 cm from the floor and at least 1m from heaters, at a temperature max 30°C, relative humidity max 80% Prior to processing bags with polymer shall be kept in production are for at least 12 hrs.
- Technology
- Plastics
- Packaging Type
- Bags
- Packing and Supply Form
Supply form: Pallets Packing: Product is packed in polyethylene bags (one bag net weight 25.00 ±0,25kg) and stacked on flat pallets with shrink film. Maximum gross weight of a bundle is 2 tons. Transport: by all modes of transport.
- Certifications and Compliance
- ISO 9001
- Plastics and Elastomers End Uses
- Bottles
- Containers
- Cosmetic Packaging
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Blow Molding
- Blown Film Extrusion
- Extrusion
- Film Extrusion
Technical data
Table 1 of 1
11 rows| Characteristic | Value | Unit |
|---|---|---|
| Density (23°C) | 955 - 961 | kg/m3 |
| Density (20°C) | 957 - 963 | kg/m3 |
| Melt Flow Index (190°C and Load of 49 N (5Kgf) | 2.3 – 3.3 | g/10 min |
| Melt Flow Index Spread Within A Batch | max. ±10 | % |
| Number of Inclusions | max. 5 | pcs |
| Weight Content of Ash | max. 0.03 | % |
| Weight Content of Volatile Substances | max. 0.09 | % |
| Tensile Yield Strength | min. 26 | MPa |
| Rupture Strength | min. 30 | MPa |
| Elongation at Break | min. 750 | % |
| Cracking Resistance | min. 30 | hours |