2MILA PE2NT11 - 9
- Chemical Family
- PolyethylenesPolyolefins
2MILA PE2NT11 - 9 is intended for production of pipes and fittings to gas distribution networks as well as pressure pipes and fittings to domestic water supply systems.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
- Pipes & Hoses
- Pipes & Plumbing
Product Families
- Polyolefins
Other characteristics
- Polymer Name
- High Density Polyethylene (HDPE)
- Melt Flow Index
- 6.0 - 8.0 g/10 min
- Processing Methods
- Extrusion
- Notes
1) Test atmosphere – oxygen, sample weight – (15 ± 2) mg. 2) it is permissible to carry out testing at 210 0 С or 220 0 С . In the event of disagreement, tests shall be carries out at 200 0 С . 3) Test result is not a rejecting one. 4) Water content shall be determined if weight content of volatile substances exceeds the set standard. At that, the difference between the obtained value of weight content of volatile substances and that of weight content of water shall not exceed 350 mg/kg. Requirement to water content in the composition is applied to the manufacturer at production stage, to the consumer – at processing stage (if water content exceeds the limiting value, then the material has to be dried prior to use). 5) In the event of disagreement, test samples shall be manufactured by pressing method. 6) 50% n-decane (98%) and 50% 1,3,5- trimethylbenzene by weight. 7) Internal pressure – 9.2 bar, test medium – water in water.
- Markets
- Agriculture & Feed
- Building & Construction
- Storage
Polyethylene shall be stored in enclosed dry space preventing from direct sunlight on shelves or pallets at least 5 cm from the floor and at least 1m from heaters, at a temperature max 30°C, relative humidity max 80% Prior to processing bags with polymer shall be kept in production are for at least 12 hrs.
- Technology
- Plastics
- Packaging Type
- Bags
- Packing and Supply Form
Supply form: Pallets Packing: Product is packed in polyethylene bags (one bag net weight 25.00 ±0,25kg) and stacked on flat pallets with shrink film. Maximum gross weight of a bundle is 2 tons. Transport: by all modes of transport.
- Certifications and Compliance
- ISO 9001
- Plastics and Elastomers End Uses
- Fittings
- Natural Gas Distribution
- Pipes
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
Technical data
Table 1 of 1
17 rows| Characteristic | Value | Unit |
|---|---|---|
| Density (23°C) | min. 930 | kg/m3 |
| Density (20°C) | 956 – 962 | kg/m3 |
| Thermal Stability (Oxidation Induction Time)1), 200°C2) | min. 20 | minutes |
| Melt Flow Index (Mfi) (190°C and Load of 212 N (2,16Kgf) | 6 - 8 | g/10 min |
| Melt Flow Index (Mfi) (190°C, at Load of 49 N (5Kgf) | min. 0.12 | g/10 min |
| Melt Flow Index Spread (Mfi 5, Within A Batch) | ±20 | % |
| Weight Content of Volatile Substances3) | max. 350 | mg/kg |
| Water Content4) | max. 300 | mg/kg |
| Weight Content of Carbon Black (Within Limits) | 2.0 - 2.5 | % |
| Carbon Black Distribution5) (Type А.1, А.2, А.3 Or В) (Class) | max. 3 | — |
| Gas Condensate (Gas Components, Resistance6, 80°С and Circular Stress 2.0 Mpa, On Pipes D32 Mm Sdr 11, Test Duration of 20 H) | Without Destruction | MPa |
| Resistance To Rapid Crack Propagation (Critical Pressure Рс, Mpa) (Е ≥ 20Mm) (Dn: 225 Mm Sdr 11) For C=2 (Strength Factor) | МОР/2.4 - 0.072 | MPa |