2MILA PE2NT11 - 285D
- Chemical Family
- PolyethylenesPolyolefins
2MILA PE2NT11 - 285D is intended for production of pipes and fittings, including domestic water supply systems,compositions for marking stripes, blow-molded articles as well as for production of heavy duty PE films with minimum thickness of 20 μm m.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
- Pipes & Hoses
- Pipes & Plumbing
Product Families
- Polyolefins
Other characteristics
- Polymer Name
- High Density Polyethylene (HDPE)
- Melt Flow Index
- 6.0 - 11.0 g/10 min
- Processing Methods
- Extrusion, Film Extrusion
- Notes
Note: Parameter 6 shall be determined by the processer when introducing polyethylene into production in order to make a decision on the necessity of preliminary drying and its modes. Test result is not a rejecting one.
- Markets
- Agriculture & Feed
- Building & Construction
- Storage
Polyethylene shall be stored in enclosed dry space preventing from direct sunlight on shelves or pallets at least 5 cm from the floor and at least 1m from heaters, at a temperature max 30°C, relative humidity max 80% Prior to processing bags with polymer shall be kept in production are for at least 12 hrs.
- Technology
- Plastics
- Packaging Type
- Bags
- Packing and Supply Form
Supply form: Pallets Packing: Product is packed in polyethylene bags (one bag net weight 25.00 ±0,25kg) and stacked on flat pallets with shrink film. Maximum gross weight of a bundle is 2 tons. Transport: by all modes of transport.
- Certifications and Compliance
- ISO 9001
- Plastics and Elastomers End Uses
- Film
- Fittings
- Natural Gas Distribution
- Pipes
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Film Extrusion
Technical data
Table 1 of 1
12 rows| Characteristic | Value | Unit |
|---|---|---|
| Density (23°C) | 947 - 950 | kg/m3 |
| Density (20°C) | 949 - 952 | kg/m3 |
| Melt Flow Index (190°C and Load of 21.6 Kgf) | 6 – 11 | g/10 min |
| Melt Flow Index Spread (Mfi 21,6, Within A Batch) | max. ± 10 | — |
| Tensile Yield Strength | min. 20 | MPa |
| Elongation at Break | min. 600 | % |
| Weight Content of Volatile Substances | max. 350 | mg/kg |
| Thermal Stability (200°C) | min. 20 | minutes |
| Durability at Constant Internal Pressure at 80 °С, at Initial Stress In Pipe Wall 4.0 Mpa (On Pipes D110 Sdr 11), H | min. 165 | MPa |
| Durability at Constant Internal Pressure at 80 °С, at Initial Stress In Pipe Wall 2.8 Mpa (On Pipes D110 Sdr 11),H | min. 1000 | MPa |
| Durability at Constant Internal Pressure at 20 °С On Pipes D32 Mm Sdr 11 at Initial Stress, H 12.4 Mpa | 100.0 | MPa |
| Durability at Constant Internal Pressure at 20 °С On Pipes D32 Mm Sdr 11 at Initial Stress, H 11.6 Mpa | 2500.0 | MPa |