2MILA 11503 - 070
- Chemical Family
- PolyethylenesPolyolefins
2MILA 11503 - 070 is intended for food contact, for manufacture of toys and articles approved for packing and sealing of medicines. To be used for covering the articles allowed for food contact, for lamination by extrusion of such materials as paper, aluminum foil, cardboard etc. To be used as well for casting of small-sized articles (covers, caps, toys).
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
- Consumer Goods — Sports & Recreation
- Healthcare Packaging
- Non-Food Consumer Packaging
Product Families
- Polyolefins
Other characteristics
- Polymer Name
- Low Density Polyethylene (LDPE)
- Processing Methods
- Extrusion, Film Extrusion
- Markets
- Consumer Goods
- Printing & Packaging
- Storage
Polyethylene shall be stored in enclosed dry space preventing from direct sunlight on shelves or pallets at least 5 cm from the floor and at least 1m from heaters, at a temperature max 30°C, relative humidity max 80%. Prior to processing bags with polymer shall be kept in production are for at least 12 hrs.
- Technology
- Plastics
- Packaging Type
- Bags
- Labeling Claims
- Food Contact Acceptable
- Packing and Supply Form
Supply form: Pallets Packing: Product is packed in polyethylene bags (one bag net weight 25.00 ±0,25kg) and stacked on flat pallets with shrink film. Maximum gross weight of a bundle is 2 tons. Transport: by all modes of transport.
- Certifications and Compliance
- ISO 9001
- Plastics and Elastomers End Uses
- Caps
- Medical Packaging
- Toys
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Film Extrusion
Technical data
Table 1 of 1
7 rows| Characteristic | Value | Unit |
|---|---|---|
| Density | 0.9180 ± 0.001 | g/cm3 |
| Melt Flow Index ((Nominal Value) With A Tolerance), | 7.0 ± 15 | %/g/10 min |
| Melt Flow Index Spread Within A Batch | max. ± 5 | % |
| Number of Inclusions | max. 2 | pcs |
| Tensile Yield Strength | min. 9.3 | MPa |
| Rupture Strength | min. 9.8 | % |
| Elongation at Break | min. 450 | % |