To catalogue
2MILA 153 - 10K
- Chemical Family
- PolyethylenesPolyolefins
2MILA 153 - 10K is intended for application of insulation, sheaths and protective covering to wires and cables by means of extrusion.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
Electrical & Electronics — Wire & Cable
- Jacketing & Insulation
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Polymer Name
- Low Density Polyethylene (LDPE)
- Processing Methods
- Cable Extrusion, Extrusion
- Markets
- Electrical & Electronics
- Storage
Polyethylene shall be stored in enclosed dry space preventing from direct sunlight on shelves or pallets at least 5 cm from the floor and at least 1m from heaters, at a temperature max 30°C, relative humidity max 80%. Prior to processing bags with polymer shall be kept in production are for at least 12 hrs.
- Technology
- Plastics
- Packaging Type
- Bags
- Packing and Supply Form
Supply form: Pallets Packing: Product is packed in polyethylene bags (one bag net weight 25.00 ±0,25kg) and stacked on flat pallets with shrink film. Maximum gross weight of a bundle is 2 tons. Transport: by all modes of transport.
- Certifications and Compliance
- ISO 9001
- Plastics and Elastomers End Uses
- Cables
- Wires
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Cable Extrusion
- Extrusion
Technical data
Table 1 of 1
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Density | Not specified | g/cm3 |
| Melt Flow Index (Load of 2.16 Kgf Within The Limits) | 0.21 ÷ 0.39 | g/10 min |
| Melt Flow Index Spread Within A Batch | max. ± 8 | % |
| Thermo-Oxidative Stability | min. 8 | hours |
| Photo-Oxidative Stability, Hour, Minimum | min. 500 | hours |
| Stress Cracking Resistance | min. 1000 | hours |
| Tensile Yield Strength | min. 9.8 | MPa |
| Rupture Strength | min. 13.7 | MPa |
| Elongation at Break | min. 600 | % |