2MILA PE2NT22 - 12
- Chemical Family
- PolyethylenesPolyolefins
2MILA PE2NT22 - 12 is intended for further processing by injection molding into articles for household and domestic use with increased cracking resistance such as bottle caps, box covers, caps, boxes, containers, trays, housewares, injection syringe parts and needles, toys.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
- Consumer Goods — Housewares
- Consumer Goods — Sports & Recreation
- Disposable Ware
- Industrial & Transport Packaging
- Non-Food Consumer Packaging
Product Families
- Polyolefins
Other characteristics
- Polymer Name
- High Density Polyethylene (HDPE)
- Melt Flow Index
- 6.0 - 9.0 g/10 min
- Processing Methods
- Injection Molding
- Markets
- Consumer Goods
- Healthcare & Pharma
- Printing & Packaging
- Storage
Polyethylene shall be stored in enclosed dry space preventing from direct sunlight on shelves or pallets at least 5 cm from the floor and at least 1m from heaters, at a temperature max 30°C, relative humidity max 80% Prior to processing bags with polymer shall be kept in production are for at least 12 hrs.
- Technology
- Plastics
- Packaging Type
- Bags
- Material Features
- Crack Resistant
- Packing and Supply Form
Supply form: Pallets Packing: Product is packed in polyethylene bags (one bag net weight 25.00 ±0,25kg) and stacked on flat pallets with shrink film. Maximum gross weight of a bundle is 2 tons. Transport: by all modes of transport.
- Certifications and Compliance
- ISO 9001
- Plastics and Elastomers End Uses
- Caps
- Containers
- Household Goods
- Hypodermic Syringe Parts
- Toys
- Trays
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 1
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Density (23°C) | 958 - 965 | kg/m3 |
| Density (20°C) | 960 - 966 | kg/m3 |
| Melt Flow Index (190°C and Load of 2,16 Kg) | 6.0 - 9.0 | g/10 min |
| Melt Flow Index Spread Within A Batch | max. ±15 | % |
| Number of Inclusions | max. 10 | pcs |
| Melt Flow Ratio (Mfi 21.6 / Mfi 2.16) | 20 - 35 | — |
| Tensile Yield Strength | min. 28 | MPa |
| Rupture Strength | min. 17 | % |
| Weight Content of Pallets Less Than 2Mm and More Than 5 To 8 Mm In Size | max. 1 | — |