To catalogue
2MILA РС-005
- Chemical Family
- Polycarbonate (PC)
2MILA РС-005 is intended for manufacturing of industrial-used products by extrusion and injection molding, such as locking panels and articles in contact with food and drinking water.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Other Industrial Applications
Printing & Packaging — Packaging
- Food & Beverage Packaging
Product Families
Plastics — Engineering & Specialty Polymers
- Polycarbonates
Other characteristics
- Polymer Name
- Поликарбонат (PC)Polycarbonate (PC)
- Flexural Modulus
- 2250.0 - 2250.0 MPa
- Processing Methods
- Extrusion, Injection Molding
- Markets
- Industrial
- Printing & Packaging
- Storage
Polycarbonates shall be stored in enclosed dry space preventing from direct sunlight on shelves or pallets at least 5 cm from the floor and at least 1m from heaters, at a temperature max 35°C.
- Technology
- Plastics
- Packaging Type
- Bags
- Super Sacks
- Labeling Claims
- Food Contact Acceptable
- Material Features
- Drinking Water Contact Acceptable
- High Viscosity
- Packing and Supply Form
Supply form: Pallets Packing: Product is packed in polymer bags. The bags neck should be sealed on. Polycarbonates are also packaged in sealed soft containers for bulk solids. Packages should be tightly sewed. Polycarbonate weight in bag should be 25.00 ±0,25kg. In bigbag 750±3.75 kg, 850±4.25 kg, 1000±5.0 kg. Transport: by all modes of transport.
- Certifications and Compliance
- ISO 9001
- Plastics and Elastomers End Uses
- Industrial Applications
- Industrial Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Injection Molding
Technical data
Table 1 of 1
16 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Flow Index (1.2 Kgf Load, 300°C) | 5.0 ± 1.0 | g/10 min |
| Melt Flow Index Spread Within A Batch (All Spot Samples Shall Comply With Value) | max. 1 | % |
| Number of Visible Impurities (Inclusions) | max. 5 | balls/100g |
| Haze | max. 0.8 | % |
| Transmission Factor | min. 89 | % |
| Tensile Yield Strength | min. 60 | MPa |
| Elongation at Break | min. 120 | % |
| Cross-Bending Stress at Max. Sample Load | min. 90 | MPa |
| Flexural Modulus | min. 2250 | MPa |
| Izod Impact Strength | min. 75 | kJ/m2 |
| Compression Stress at Yield | min. 76 | MPa |
| Vicat Softening Temperature | min. 150 | °C |