LNP™ ELCRES™ FXE9111T
SABIC's Specialties Business ELCRES FXE9111T PC Siloxane copolymer resin is an injection molding grade. Non-chlorinated, non-brominated flame retardant. This resin offers good low temperature (-10 C) ductility in combination with high flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. Available for VisualFx capability in opaque “Illuminate” colors. ELCRES FXE9111T resin may be an excellent candidate for a broad range of applications, including but not limited to Automobile, Appliance, Electronics, etc.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Housewares
- Consumer Goods — Sports & Recreation
- Interior
- Consumer Electronics
- Displays
- Lighting
- Industrial & Transport Packaging
- Non-Food Consumer Packaging
- Housings & Enclosures
Product Families
- High Performance Thermoplastics
- Polycarbonates
Other characteristics
- Brand
- LNP™ ELCRES
- Polymer Name
- Polycarbonate-Siloxane Copolymer
- Flexural Modulus
- 2190.0 - 2190.0 MPa
- Additives Included
Flame Retardant, Mold Release Agent, UV Stabilizer; Flame Retardant; Mold Release Agent; UV Stabilizer
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Color
- Custom
- Transparent
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Printing & Packaging
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- Material Features
- Excellent Aesthetics
- Flame Retardant
- Good Aesthetics
- Good Colorability
- Good Mold Release
- Good Processability
- Good Surface Appearance
- High Ductility
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Automotive Applications
- Automotive Interior Parts
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Covers
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
18 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 57 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 54 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 5 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 92 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 2190 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 90 | MPa | ASTM D790 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 89 | MPa | ASTM D790 |
| Flexural Stress (at 5% strain, 1.3 mm/min, 50 mm span) ¹¹ | 85 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2180 | MPa | ASTM D790 |
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 58 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 5 | % | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 52 | MPa | ISO 527 |
Table 2 of 6
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.2 | — | ASTM D792 |
| Density ¹¹ | 1.201 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.11 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.04 | % | ISO 62-4 |
| Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹ | 19.5 | g/10 min | ASTM D1238 |
| Melt Volume Rate (at 300°C, 1.2 kg) ¹¹ | 18.3 | cm³/10 min | ASTM D1238 |
| Mold Shrinkage (flow) ᵍ ¹¹ | 0.66 | % | SABIC method |
| Mold Shrinkage (xflow) ᵍ ¹¹ | 0.73 | % | SABIC method |
Table 3 of 6
15 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 119 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 107 | °C | ASTM D648 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 119 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 107 | °C | ISO 75/Af |
| Coefficient of Thermal Expansion (at -40°C to 95°C, flow) ¹¹ | 0.000075 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 95°C, xflow) ¹¹ | 0.000083 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹ | 0.000081 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 80°C, xflow) ¹¹ | 0.000086 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature (Rate A/50) ¹¹ | 132 | °C | ASTM D1525 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 126 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 126 | °C | ASTM D1525 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 125 | °C | ISO 306 |
Table 4 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 2150 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 0°C) ¹¹ | 500 | J/m | ASTM D256 |
| Izod Impact (Notched, at 23°C) ¹¹ | 777 | J/m | ASTM D256 |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 57 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 180 | kJ/m² | ISO 180/1U |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 130 | kJ/m² | ISO 179/1eU |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 59 | kJ/m² | ISO 179/1eA |
Table 5 of 6
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 90 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 250 - 285 | °C |
| Nozzle Temperature ⁷ | 250 - 285 | °C |
| Front - Zone 3 Temperature ⁷ | 250 - 285 | °C |
| Middle - Zone 2 Temperature ⁷ | 250 - 285 | °C |
| Rear - Zone 1 Temperature ⁷ | 250 - 285 | °C |
| Mold Temperature ⁷ | 50 - 90 | °C |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 2.0 | mm | UL 94 |