LNP™ LUBRICOMP™ Compound RN001

Chemical Family: Polyamides

SABIC's Specialties Business LNP LUBRICOMP RN001 compound is based on Nylon 6/6 resin containing Molybdenum diSulfide (MoS2). Added features of this grade include: Wear Resistant This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Lawn & Garden
Consumer Goods — Sports & Recreation

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: LNP™ LUBRICOMP™ Compound
Polymer Name: Polyamide 66 (PA 66)
Fillers Included: Molybdenum Disulfide
Flexural Modulus: 2600.0 - 2600.0 MPa
Additives Included: Mold Release Agent
Processing Methods: Injection Molding
Note: ⁷ Параметры литья под давлением указаны только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных изделий и газовое литье.; ¹¹ Информация, указанная в технических паспортах, должна использоваться только для целей выбора материала и не должна применяться в качестве спецификации или использоваться для проектирования деталей или пресс-форм.; ᵖ Рейтинги UL, указанные в техническом паспорте, могут не охватывать весь диапазон толщин и цветов. Для получения подробной информации, пожалуйста, обратитесь к карточке UL Yellow Card.
Markets: Building & Construction
Consumer Goods
Electrical & Electronics
Personal Care
Printing & Packaging
Flame Rating: UL 94 HB
Technology: Plastics
Labeling Claims: No Added PFAS
Material Features: Friction Resistant
Good Mold Release
No Added PFAS
Wear Resistant
Certifications and Compliance: UL 94
Plastics and Elastomers End Uses: Appliances
Building Materials
Cell Phones
Commercial Appliance
Computer Components
Consumer Applications
Containers
Displays
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

6 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break, 5 mm/min) ¹¹	77	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	5.4	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	6.6	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	3200	MPa	ISO 527
Flexural Stress (Break, 2 mm/min) ¹¹	91	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	2600	MPa	ISO 178

Table 2 of 6

1 row

Characteristic	Value	Unit	Method
Density ¹¹	1.16	g/cm³	ISO 1183

Table 3 of 6

4 rows

Characteristic	Value	Unit	Method
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.00009	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.0001	1/°C	ISO 11359-2
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80104, sp=64mm) ¹¹	232	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	64	°C	ISO 75/Af

Table 4 of 6

2 rows

Characteristic	Value	Unit	Method
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	50	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80104, at 23°C) ¹¹	5	kJ/m²	ISO 180/1A

Table 5 of 6

10 rows

Characteristic	Value	Unit
Drying Temperature ⁷	80	°C
Drying Time ⁷	4	Hrs
Maximum Moisture Content ⁷	0.15 - 0.25	%
Melt Temperature ⁷	275 - 290	°C
Front - Zone 3 Temperature ⁷	295 - 305	°C
Middle - Zone 2 Temperature ⁷	280 - 295	°C
Rear - Zone 1 Temperature ⁷	265 - 275	°C
Mold Temperature ⁷	80 - 95	°C
Back Pressure ⁷	0.2 - 0.3	MPa
Screw Speed ⁷	30 - 60	rpm

Table 6 of 6