E-Seal 1007
E-Seal 1007 is a high performance corrosion resistant polymer sealer that provides over 300 hours of salt spray protection to white rust and 500 hours of salt spray protection to red rust when applied over zinc plated (zinc plating thickness 0.0003") parts in E-Brite Ultra Alk or E-Brite Ultra Chlor plating baths and chromated in E-Chrome hexavalent or trivalent chromates. E-Seal 1007 is a concentrated liquid that is diluted to 20-30% by volume with tap water.
Properties
- Physical Form
- Liquid
Product families
- Primers & Sealers
Other characteristics
- Brand
- E-Seal
- Features
Corrosion Resistant, Excellent Performance, Excellent Salt Spray Resistance
- Product Type
- Sealer
- Carrier
- Water
- Caution
This material is alkaline. Do not get in eyes, on skin or on clothing. Do not breathe mists. Do not take internally. When handling, wear goggles or face shield. While making up solutions, or adding to a solution, add slowly to surface of solution to avoid spattering. In case of contact immediately flush skin or eyes with plenty of water for at least 15 minutes. For eyes, call physician. Do not mix E-Seal 1007 with acidic materials or any other chemical substances.
- Markets
- Paints & Coatings
- PACKAGING
5 gallon and 55 gallon plastic, non-returnable containers. Keep lid on when not in use.
- Applications
Paints & Coatings — Other Paints & Coatings Applications
- Technology
- Ready-to-Use Products
- Technical Details
Solution Make Up Fill the tank to 2/3 of the way with water. Carefully pour E-Seal 1007 to obtain the desired concentration – avoid spattering. Wear safety glasses, gloves and apron. Add water to working level.. Processing Procedure 1. Zinc or cadmium plated surfaces 2. Thorough cold water rinse will prolong the life of chromate. a.) Optional 1% Sulfuric Acid to neutralize residual plating solution with barrel processed work. b.) Cold water rinse 3. Immersion in E-Chrome or E-PASSivate (see respective product data sheet). 4. Cold water rinse 5. E-Seal 1007. For optimum corrosion resistance the immersion time must be kept to a minimum. Maximum immersion time – 60 seconds. 6. Hot air dry. Optimum corrosion resistance will be obtained if the temperature of the hot air is kept below 150F for hexavalent chromates. Analysis is by refractive index: Refractive index X 3.33 = % of E-Seal 1007.
- HIGHLIGHTS
High Performance Multi-Purpose Sealer for Zinc/Chromated Surfaces Traditional silicate seals work in most applications with limitations. E-Seal 1007 can be applied to all E-Chrome hexavalent chromates clear, yellow and black plus all E-PASSivate trivalent chromates offering 3-5 times longer corrosion protection to white corrosion per ASTM B-117. E-Seal 1007 does not significantly change the thickness of the plated part, works over different chromate films and is utilized in the final dip. Equipment Tanks should be constructed of polypropylene, PVC, Koroseal lined carbon steel or stainless steel.
- Ready to Use Product Features
- Corrosion Resistant
- Excellent Performance
- Excellent Salt Spray Resistance