OPTOOL DSX-E
- CASE Ingredients Features
- High DurabilityOil ResistanceWater Resistance
- Chemical Family
- Fluoropolymers
OPTOOL DSX-E is a liquid solution tailored for surfaces, particularly glass and SiO2-coated surfaces. This product offers multiple benefits, such as water and oil resistance, anti-adhesion against oils like fingerprints, and reduced sliding angles, especially concerning oils. Additionally, it ensures low friction and durability and facilitates ice suppression with easy removal. Designed for ease of use, it is compatible with coated surfaces and glass, all while maintaining an odor-free profile.
Properties
- Physical Form
- Liquid
Identification
- CASE Ingredients Functions
- Anti-Fouling Agent
Product families
- Surface Modifiers
Other characteristics
- Brand
- OPTOOL
- Features
High Durability, Oil Resistance, Water Resistance
- Functions
- Anti-Fouling Agent
- Labeling Claims
- Odor-free
- Note
The following Typical Properties was measured on DSX E coated Gorilla Glass surface and are not suitable for specification purposes.; (*2) Irradiation time to keep water contact angle above 100 degrees. UV source: UV B313, Irradiance ( at 313nm):0.63W/m2; (*3) Irradiation time to keep water contact angle above 100 degrees (SAE J2527); (*4) Maximum rubbing cycles to keep water contact angle above 100 degrees. Conditions: Steel wool #0000, Load: 1 Kgf/cm2, Stroke: 6cm, Speed: 60rpm; (*5) Equipment: LabthinkFPT-1, Load: 200g, Speed: 200mm/min, friction material: paper; (*6) Water contact angle in Air 130 after 6days passage.; (*7) Water contact angle in Air 85°C°C/85%RH after 6days passage.; (*8) Water contact angle in 1.0mass% HClaq. 25 after 4days passage.; (*9) Water contact angle in 4.0mass% NaOHaq. 25 after 4hours passage.
- Technology
- CASE Ingredients
- HIGHLIGHTS
OPTOOL DSX E is especially effective on glass and surfaces coated with SiO2. It adds the following characteristics to the surfaces:; Water and oil resistant.; Anti adhesion of oils like fingerprints and its easy removability.; Low friction surfaces.; Durability.; Sliding angle reduction, especially effective for oils.; Non cohesiveness.; Ice suppression and easy removability.; It is simply used and contributes to rapid processing.
- Packing Specification
- 100g
- Safety Information
Be sure to read the notes on SDS and labels before use.. This product is intended for general industry, and therefore its adequacy and safety as a raw material for medical purposes cannot be guaranteed.
- Compatible Substrates and Surfaces
- Coated Surfaces
- Glass
Technical data
Table 1 of 1
15 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Acid Resistant (*8) | 107 | Degree | — |
| Base Resistant (*9) | 59 | Degree | — |
| Cleanability | Excellent | — | — |
| COF (*5) | 0.07 | — | — |
| Critical Surface Tension | 13 | mN/m | — |
| Haze | 0.25 | % | — |
| QUV Durability (*2) | 72 | h | — |
| Sliding Angle (n-hexadecane) | 6 | Degree | — |
| Sliding Angle (Water) | 8 | Degree | — |
| Steel Wool Abrasion Durability (*4) | 6000 | cycle | — |
| Tendency for Fingerprint Transfer | Better | — | — |
| Water Contact Angle | 115 | Degree | — |