Polyflon PTFE E-3705S21R
- Chemical Family
- Fluoropolymers
Polyflon PTFE E-3705S21R is a water-based PTFE topcoat used in waterborne coatings and belongs to the fluoropolymer chemical family. This ready-to-use product, available in liquid form, boasts features like heat resistance and non-stick properties. Ideal for various applications, it stands out as a reliable choice for achieving excellent surface characteristics.
Properties
- Physical Form
- Liquid
Product families
- Top Coats
Other characteristics
- Brand
- Polyflon
- Features
- Heat Resistance, Non Stick
- Product Type
- Top Coat, Waterborne Coating
- Top Coat
- Waterborne Coating
- Note
1. The The coating film was evaluated (all Properties) with a test piece below.; Substrate: Aluminum plate roughened with Tosa Emely Extra #80/#100=50/50; Primer: EK 1909S21R, approximately 10μm thick; Topcoat: Approximately 20μm thick; 2. Corrosion resistance test (Oden soup stock test) : 5 cycles of the following; SB Oden soup stock is dissolved into 1L water and boiled for 1 hour Hot insulation for 7 hours Left unattended for 16 hours; 3. The above values in properties are typical and not guaranteed.
- Technology
- Ready-to-Use Products
- HIGHLIGHTS
Polyflon PTFE E - 3705S21R is a water based PTFE topcoat.; It makes a green topcoat layer displaying heat resistance and non stick property.
- Ready to Use Product Features
- Heat Resistance
- Non Stick
- Safety Information
Be sure to read the notes on SDS and labels before use.. This product is intended for general industry, and therefore its adequacy and safety as a raw material for medical purposes cannot be guaranteed.
Technical data
Table 1 of 2
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Film Appearance | Green | — |
| pH | 9 | — |
| Solid Content | 42 | mass% |
| Specific Gravity of Coating | approx. 1.3 - 1.4 | — |
| Viscosity | 270 | cP |
Table 2 of 2
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Boiled Water Resistance (for 100 hours at 90~95°C) | Good | — | — |
| Corrosion Resistance | Good | — | Corrosion Resistance Test ² |
| Cross Cut Adhesion (Stripping with cellophane tape,10 times) | 100/100 | — | JIS K5400 8.5 |
| Gloss | 15 - 25 | — | JIS K5400 7.6 |
| Hot Oil Resistance (for 16 hours, at 260°C) | Good | — | — |
| Pencil Hardness (at 200°C, Stripping hardness of base material) | B - HB | — | JIS K6894 |
| Pencil Hardness (at 25°C, Stripping hardness of base material) | H - 2H | — | JIS K6894 |
| Salt Spray | Good | — | JIS Z2371 |
| Taber Abrasion (at 25°C, CS 17, 1kg, 1000 rounds) | 6 - 12 | mg/1000 rounds | — |