Neoflon PFA TC-7109BK
- Chemical Family
- Fluoropolymers
Neoflon PFA TC-7109BK is identified as a solventborne coating that exhibits features such as wear resistance and low friction. Specifically designed for application on slides, Neoflon PFA TC-7109BK is a liquid-form coating ensures durability and smooth functioning in various scenarios.
Properties
- Physical Form
- Liquid
Product families
- Protective Coatings
Other characteristics
- Brand
- Neoflon
- Features
- Low Friction, Wear Resistant
- Product Type
- Solventborne Coating
- Application Area
- Slides
- Note
The above values in properties are typical and not guaranteed.
- Technology
- Ready-to-Use Products
- HIGHLIGHTS
Polyflon PTFE TC - 7100 grade is a solvent based PTFE coating.; Polyflon PTFE TC - 7109BK makes a black coating layer displaying low friction and excellent wear resistance.; It is good for sliding component.
- Ready to Use Product Features
- Low Friction
- Wear Resistant
- Safety Information
Be sure to read the notes on SDS and labels before use.. This product is intended for general industry, and therefore its adequacy and safety as a raw material for medical purposes cannot be guaranteed.
Technical data
Table 1 of 2
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Contact Angle (Hexadecane, at 25°C) | 49 – 52 | Degree | Contact Angle Meter |
| Contact Angle (Water, at 25°C) | 102 – 106 | Degree | Contact Angle Meter |
| Film Appearance | Black | — | — |
| Friction Coefficient (Bauden leben type, Steel ball 8mmφ, Linear velocity 0.27cm/s, Loading 1.0kg) | 0.04 – 0.07 | — | Bauden leben steel sheet |
| Maximum Temperature | 220 | °C | — |
| Pencil Hardness (at 25°C, after immersed in boiled water for 500hours) | 3 | H | Mitsubishi Uni |
| Solid Content | 21 | % | — |
| Specific Gravity | 1.04 | — | — |
| Viscosity (at 25℃) | 29 | sec | Ford Cup No.4 |
| Wear Resistance Sliding Abrasion (with SUS23B, 55.9kPa, 2.3m/s, 10 minutes) | 0.1 – 0.2 | mg/cm² | — |
| Wear Resistance Taber Abrasion (at 25°C, CS 17, 1kgf, 1000 rounds) | 12 – 20 | mg/1000 rounds | — |
Table 2 of 2
6 rows| Characteristic | Value |
|---|---|
| Chemical Resistance (for 16hours, at 25°C, Hydrochloric acid) | No change |
| Chemical Resistance (for 16hours, at 25°C, Methanol) | Not possible (swelling) |
| Chemical Resistance (for 16hours, at 25°C, Nitric acid) | No change |
| Chemical Resistance (for 16hours, at 25°C, Sodium hydroxide) | Not possible (swelling) |
| Chemical Resistance (for 16hours, at 25°C, Sulfuric acid) | No change |
| Chemical Resistance (for 16hours, at 25°C, Xylene) | Not possible (swelling) |