DAI-EL G-704
- Chemical Family
- Fluoropolymers
DAI-EL G-704, available in solid form, features good fluidity and is odorless. Targeting automotive and industrial applications, it excels in powertrain and equipment parts. With heat cure as its preferred method, this product is soluble in lower ketones and esters, ensuring reliable performance in components like fuel entrance cover seals and O rings.
Properties
- Physical Form
- Solid
Product families
Applications
- Powertrain & UTH
- Equipment & Parts
Product Families
- Fluoroelastomers
Other characteristics
- Brand
- DAI-EL
- Features
- Good Fluidity, Odorless
- Polymer Name
- Fluoroelastomer (FKM)
- Processing Methods
- Injection Molding, Transfer Molding
- Note
*1 The above values are representative and not guaranteed.; *2 [Formula] DAI-EL G-704: 100 phr, MT carbon black (N990): 20 phr, Calcium hydroxide: 6 phr, Magnesium Oxide (high-active): 3 phr, [Curing condition] Press cure: 10min at 170°C, Oven cure: 24hrs at 230°C.; *3 P-24 O-ring.
- Markets
- Automotive & Transportation
- Industrial
- Soluble In
- Lower ketones and esters
- Cure
- Heat Cure
- Technology
- Elastomers
- Material Features
- Good Fluidity
- Odorless
- HIGHLIGHTS
DAI-EL G-704 is a cure-incorporated copolymer of vinylidene fluoride and hexafluoropropylene which has good fluidity of molding.. It is suitable for injection molding and transfer molding.
- Packing Specification
- 20 Kg
- Plastics and Elastomers End Uses
- Fuel Entrance Cover Seal
- O Rings
- Safety Information
Be sure to read the Safety Data Sheet (SDS) and precautions on the label before using.. This product has been developed for industrial purpose and we shall not guarantee the safety if used for any other purposes. If it is going to be used for medical or food applications, please contact us in advance.
- Plastics and Elastomers Processing Methods
- Injection Molding
- Transfer Molding
Technical data
Table 1 of 2
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Fluorine Content | 66 | mass% | — |
| Mooney Viscosity (ML₁₊₁₀) (at 100°C) | 47 | MU | ASTM D1646 |
| Mooney Viscosity (ML₁₊₁₀)(at 121°C) | 30 | MU | ASTM D1646 |
| Specific Gravity (at 23°C) | 1.81 | — | ASTM D792 |
Table 2 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| 100% Tensile Stress*² | 3.5 | MPa | ASTM D412 |
| Compression Set (70hours at 200°C, 25% Compression*³)*² | 22 | % | — |
| Elongation (at break)*² | 240 | % | ASTM D412 |
| Hardness (at 3 sec)*² | 67 | Shore A | ASTM D2240 |
| Hardness (at Peak)*² | 71 | Shore A | ASTM D2240 |
| Low Temperature Retraction (TR10)*² | -18 | °C | ASTM D1329 |
| Tensile Strength*² | 13.4 | MPa | ASTM D412 |