Daikin Industries, Ltd.DAI-EL G-607
DAI-EL G-607 is a cure-incorporated terpolymer composed of vinylidene fluoride, tetrafluoroethylene, and hexafluoropropylene, designed for compression and transfer molding. Renowned for its exceptional cold-temperature flexibility, this material is targeted for applications within the automotive, transportation, and industrial sectors. Specifically, it finds utility in automotive fuel lines, fuel hoses, and O rings, serving key roles in fuel systems, powertrains, and equipment and parts. Available in pellet, sheet, and solid forms, it stands out for its odorless nature.
Brand:
- DAI-EL
Features:
- Low Temperature Flexibility, Odorless
Polymer Name:
- Fluoroelastomer (FKM)
Processing Methods:
- Compression Molding, Transfer Molding
Note:
- *¹ The above values are representative and not guaranteed.
- *2 [Formula] DAI-EL G-607: 100 phr, MT carbon black (N990): 20 phr, Calcium hydroxide: 6 phr, Magnesium Oxide (high-active): 3 phr, [Curing condition] Press cure: 10min at 170°C, Post cure: 24hrs at 230°C.
- *3 P-24 O-ring.
Markets:
- Automotive & Transportation
- Industrial
Soluble In:
- Lower ketones and esters
Technology:
- Elastomers
Physical Form:
- Pellets
- Sheets
- Solid
Chemical Family:
- Fluoropolymers
Material Features:
- Low Temperature Flexibility
- Odorless
HIGHLIGHTS:
- DAI-EL G-607 is a cure-incorporated terpolymer of vinylidene fluoride, tetrafluoroethylene and hexafluoropropylene. It is suitable for compression molding and transfer molding.
- It has excellent cold temperature flexibility.
Packing Specification:
- 20 Kg
Safety Information:
- Be sure to read the Safety Data Sheet (SDS) and precautions on the label before using.
- This product has been developed for industrial purposes and we shall not guarantee the safety if used for any other purposes. If it is going to be used for medical or food applications, please contact us in advance.
Plastics and Elastomers End Uses:
- Automotive Fuel Lines
- Fuel Hose
- O Rings
Plastics and Elastomers Processing Methods:
- Compression Molding
- Transfer Molding
Applications
Automotive & Transportation — Automotive
- Fuel Systems
- Powertrain & UTH
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Product Families
Elastomers — Specialty Elastomers
- Fluoroelastomers
| Characteristic name | Value | Unit of measurement | Test method |
| Fluorine Content | 66 | mass% | - |
| Mooney Viscosity (ML₁₊₁₀) (at 100°C) | 66 | MU | ASTM D1646 |
| Mooney Viscosity (ML₁₊₁₀) (at 121°C) | 43 | MU | ASTM D1646 |
| Specific Gravity (at 23°C) | 1.8 | - | ASTM D792 |
| Characteristic name | Value | Unit of measurement | Test method |
| 100% Tensile Stress*² | 5.9 | MPa | ASTM D412 |
| Compression Set (at 200°C,70 hours, 25% Compression*³)*² | 17 | % | - |
| Elongation (at break)*² | 220 | % | ASTM D412 |
| Hardness (at 3sec)*² | 66 | Shore A | ASTM D2240 |
| Hardness (at peak)*² | 69 | Shore A | ASTM D2240 |
| Low Temperature Retraction (TR10)*² | -19 | °C | ASTM D1329 |
| Tensile Strength*² | 17 | MPa | ASTM D412 |