Polyflon PTFE EK-3781M21R
- Chemical Family
- Fluoropolymers
Polyflon PTFE EK-3781M21R is meticulously crafted as a liquid solution, exclusively engineered for applications within the consumer goods sector. Specifically targeting appliances and electronics, this formulation stands out in its adaptability, particularly within the realm of cooking appliances, ensuring optimal functionality and longevity.
Properties
- Physical Form
- Liquid
Product families
- Top Coats
Other characteristics
- Brand
- Polyflon
- Features
- Non Stick
- Product Type
- Top Coat, Waterborne Coating
- Top Coat
- Waterborne Coating
- Application Area
- Cooking Appliances
- Note
1. The coating film was evaluated with a test piece below.; Substrate: Aluminum plate roughened with Tosa Emely Extra #80/#100=50/50; Primer: EK 1909S21R, approximately 10μm thick; Topcoat: Approximately 20μm thick; 2. Corrosion resistance test (Oden soup stock 5 cycles of the following; SB Oden soup stock is dissolved into 1L water and boiled for 1 hour Hot insulation for 7 hours Left unattended for 16 hours; 3. The above values in properties are typical and not guaranteed.
- Markets
- Consumer Goods
- Applications
- Consumer Goods — Appliances & Electronics
- Technology
- Ready-to-Use Products
- HIGHLIGHTS
Polyflon PTFE EK - 3700 grade is a water based PTFE topcoat.; Polyflon PTFE EK - 3781M21R makes a gray metallic topcoat layer displaying non stick property.; It is good for cooking appliances and kitchen appliances.
- Ready to Use Product Features
- Non Stick
- Safety Information
Be sure to read the notes on SDS and labels before use.. This product is intended for general industry, and therefore its adequacy and safety as a raw material for medical purposes cannot be guaranteed.
Technical data
Table 1 of 3
4 rows| Characteristic | Value | Unit |
|---|---|---|
| pH | 9 | — |
| Solid Content | 42 | mass% |
| Specific Gravity of Coating | approx. 1.3 - 1.4 | — |
| Viscosity | 270 | cP |
Table 2 of 3
1 row| Characteristic | Value |
|---|---|
| Film Appearance | Gray metallic |
Table 3 of 3
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Boiled Water Resistance (for 100 hours at 90~95°C) | Good | — | — |
| Corrosion Resistance | Good | — | Corrosion Resistance Test ² |
| Cross Cut Adhesion (Stripping with cellophane tape,10 times) | 100/100 | — | JIS K5400 8.5 |
| Gloss | 15 - 25 | — | JIS K5400 7.6 |
| Hot Oil Resistance (for 16 hours, at 260°C) | Good | — | — |
| Pencil Hardness (at 200°C, Stripping hardness of base material) | B - HB | — | JIS K6894 |
| Pencil Hardness (at 25°C, Stripping hardness of base material) | H - 2H | — | JIS K6894 |
| Salt Spray | Good | — | JIS Z2371 |
| Taber Abrasion (at 25°C, CS 17, 1kg, 1000 rounds) | 6 - 12 | mg/1000 rounds | — |