DAI-EL G-501NK
- Chemical Family
- Fluoropolymers
DAI-EL G-501NK, presented in sheet form, showcases excellent adhesion and mechanical properties and is odorless. Designed for automotive fuel systems, particularly fuel lines and O rings, it appears in a distinctive white color. Utilizing chemical cure and compression molding methods, this product proves its worth in automotive and transportation applications, providing reliable performance in fuel-related components.
Properties
- Physical Form
- Sheets
Product families
- Fuel Systems
- Powertrain & UTH
Other characteristics
- Brand
- DAI-EL
- Color
- White
- End Uses
- Automotive Fuel Lines, Fuel Hose, O Rings
- Features
Good Adhesion, Good Mechanical Properties, Odorless
- Polymer Name
- Fluoroelastomer (FKM)
- Tensile Strength
- 18.7 - 18.7 MPa
- Note
*1 The above values are representative and not guaranteed.; *2 [Formula] DAI-EL G-501NK: 100 phr, MT carbon black (N990): 20 phr, Magnesium Oxide (high-active): 15 phr, Valcanization agent V-3: 3 phr [Curing condition] Press cure: 20min at 160°C, Post cure: 24hrs at 200°C.; *3 P-24 O-ring.
- Markets
- Automotive & Transportation
- Soluble In
- Lower ketones and esters
- Cure
- Chemical Cure
- Technology
- Elastomers
- Product Families
- Elastomers — Parts & Shapes
- Material Features
- Good Adhesion
- Good Mechanical Properties
- Odorless
- HIGHLIGHTS
DAI-EL G-501NK is a bisphenol type terpolymer of vinylidene fluoride, tetrafluoroethylene and hexafluoropropylene which is suitable for compression molding.. It offers excellent adhesion properties to metal and mechanical properties. It is suitable for fuel hoses.
- Packing Specification
- 20 Kg
- Plastics and Elastomers End Uses
- Automotive Fuel Lines
- Fuel Hose
- O Rings
- Safety Information
Be sure to read the Safety Data Sheet (SDS) and precautions on the label before using.. This product has been developed for industrial purposes and we shall not guarantee the the safety if used for any other purposes. If it is going to be used for medical or food applications, please contact us in advance.
- Plastics and Elastomers Processing Methods
- Compression Molding
Technical data
Table 1 of 2
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Fluorine Content | 68 | mass% | — |
| Mooney Viscosity (ML₁₊₁₀)(at 121°C) | 74 | MU | ASTM D1646 |
| Mooney Viscosity (ML₁₊₁₀)(at 140°C) | 50 | MU | ASTM D1646 |
| Specific Gravity (at 23°C) | 1.84 | — | ASTM D792 |
Table 2 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| 100% Tensile Stress*² | 4.1 | MPa | ASTM D412 |
| Compression Set (70hours at 200°C, 25% Compression*³)*² | 65 | % | — |
| Elongation (at break)*² | 280 | % | ASTM D412 |
| Hardness (at 3 sec)*² | 74 | Shore A | ASTM D2240 |
| Hardness (at Peak)*² | 78 | Shore A | ASTM D2240 |
| Low Temperature Retraction (TR10)*² | -16 | °C | ASTM D1329 |
| Tensile Strength*² | 18.8 | MPa | ASTM D412 |