DAI-EL LATEX GLS-213RA
- Chemical Family
- Fluoropolymers
DAI-EL LATEX GLS-213RA is a water-based fluoroelastomer coating that, when mixed with GL-200RB for curing, produces a distinctive red layer. This coating offers exceptional elasticity, heat resistance, low friction, and chemical resistance. Specifically designed for the surface modification of elastomers and rubbers, its liquid form facilitates application and ensures compatibility with various substrates.
Properties
- Physical Form
- Liquid
Product families
- Protective Coatings
Other characteristics
- Brand
- DAI-EL
- Features
Chemical Resistant, Excellent Elasticity, Heat Resistance, Low Friction
- Product Type
- Waterborne Coating
- Compatible Substrates & Surfaces
- Elastomers & Rubbers
- Note
GLS - 213RA/GL - 200RB mixing ratio (weight) :100/5; The above values in properties are typical and not guaranteed.
- Technology
- Ready-to-Use Products
- HIGHLIGHTS
DAI EL LATEX GLS grade is a water based fluoroelastomer coating.; GL - 200RB is mixed to cure the layer before applying.; DAI EL LATEX GLS 213RA makes a red coating layer displaying elasticity, heat resistance, low friction and chemical resistance.; It is good for surface modification of elastic substrate.
- Ready to Use Product Features
- Chemical Resistant
- Excellent Elasticity
- Heat Resistance
- Low Friction
- Compatible Substrates and Surfaces
- Elastomers & Rubbers
- Safety Information
Be sure to read the notes on SDS and labels before use.. This product is intended for general industry, and therefore its adequacy and safety as a raw material for medical purposes cannot be guaranteed
Technical data
Table 1 of 2
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Film Appearance | Walnut | — |
| pH | 7.5 | — |
| Sintering Temperature | approx. 120 - 350 | ℃ |
| Solid Content | 50 | mass% |
| Viscosity | 80 | cP |
Table 2 of 2
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Contact Angle (n-hexadecane, at 25°C) | 59 | Degree | Contact Angle Meter |
| Contact Angle (Water, at 25°C) | 114 | Degree | Contact Angle Meter |
| Elongation | 200 | % | — |
| Tensile Strength | 13.5 | MPa | — |