DAI-EL GBR-6002
- Chemical Family
- Fluoropolymers
DAI-EL GBR-6002 features a solid physical form with good processability, alkali resistance, and steam resistance. It is applicable in industrial markets, particularly in oil, gas, and mining exploration and upstream. With a chemical cure method, this product is suitable for O rings and turbocharger hoses.
Properties
- Physical Form
- Solid
Product families
Applications
- Cooling & Climate
- Powertrain & UTH
- Equipment & Parts
- Exploration & Upstream
- Midstream
Product Families
- Fluoroelastomers
Other characteristics
- Brand
- DAI-EL
- Features
Acid Resistant, Alkali Resistant, Good Compression Set, Good Processability, Odorless, Steam Resistant
- Polymer Name
- Fluoroelastomer (FKM)
- Note
*1 The above values are representative and not guaranteed.; *2 [Formula] DAI EL GBR 6002: 100 phr, MT carbon black (N990): 20 phr, Triallylisocyanurate (100% active): 4 phr, 2,5 dimethyl 2,5 di(t butylperoxy)hexane (100% active): 1.5 phr, [Curing condition] Press cure: 10min@160°C, Post cure: 4hrs@180°C.; *3 P 24 O ring
- Markets
- Automotive & Transportation
- Industrial
- Soluble In
- Lower ketones and esters
- Cure
- Chemical Cure
- Technology
- Elastomers
- Benefits
DAI EL GBR 6002 is a peroxide curable copolymer of vinylidene fluoride and 2,3,3,3 tetrafluoropropylene, which provides excellent resistance to amines and bases such as engine coolants, lubricating oils, some oil & gas drilling fluids and other high pH environments.. It offers superior processability, compression set and resistance to steam and acids compared with other base resistant fluoroelastomers.
- Material Features
- Acid Resistant
- Alkali Resistant
- Good Compression Set
- Good Processability
- Odorless
- Steam Resistant
- Packing Specification
- 20kg
- Plastics and Elastomers End Uses
- O Rings
- Turbo Charger Hose
- Safety Information
Be sure to read the notes on SDS and labels before use.. This product is intended for general industry, and therefore its adequacy and safety as a raw material for medical purposes cannot be guaranteed.
Technical data
Table 1 of 2
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Compression Set (at 200°C,70 hours, 25% Compression*³) | 27 | % | — |
| Elongation (at break) | 520 | % | ASTM D412 |
| Fluorine Content | 62 | mass% | — |
| Hardness (at 3 sec) | 58 | Shore A | ASTM D2240 |
| Hardness (at Peak) | 63 | Shore A | ASTM D2240 |
| Low Temperature Retraction (TR10) | -12 | °C | ASTM D1329 |
| Mooney Viscosity (ML₁₊₁₀) (at 100°C) | 49 | MU | ASTM D1646 |
| Mooney Viscosity (ML₁₊₁₀) (at 121°C) | 25 | MU | ASTM D1646 |
| Specific Gravity (at 23°C) | 1.72 | — | ASTM D792 |
| Tensile Strength | 19.4 | MPa | ASTM D412 |
Table 2 of 2
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| 100% Tensile Stress*² | 1.7 | MPa | ASTM D412 |