DAI-EL G-8002L
- Chemical Family
- Fluoropolymers
DAI-EL G-8002L is a yellow sheet elastomer tailored for applications in the automotive, transportation, and industrial sectors. Renowned for its chemical resistance and odorless nature, this material offers good flow and moldability. Employing a chemical cure method, it is specifically designed for products like O rings and turbocharger hoses produced through extrusion and injection molding processes.
Properties
- Physical Form
- Sheets
Product families
- Cooling & Climate
- Powertrain & UTH
- Equipment & Parts
Other characteristics
- Brand
- DAI-EL
- Color
- Yellow
- End Uses
- O Rings, Turbo Charger Hose
- Features
Chemical Resistant, Good Flow, Good Moldability, Odorless
- Polymer Name
- Fluoroelastomer (FKM)
- Tensile Strength
- 22.0 - 22.0 MPa
- Note
The above values in properties are representative and not guaranteed.; *2 [Formula] DAI EL G 8002L: 100 phr, MT carbon black (N990): 20 phr, Triallylisocyanurate (70% active): 5.7 phr, 2,5 dimethyl 2,5 di(t butylperoxy)hexane (45% active): 3.3 phr, [Curing condition] Press cure: 10min at 160°C, Post cure: 4hrs at 180°C.; *3 P 24 O ring.
- Markets
- Automotive & Transportation
- Industrial
- Soluble In
- Lower ketones and esters
- Cure
- Chemical Cure
- Technology
- Elastomers
- Product Families
- Elastomers — Parts & Shapes
- Material Features
- Chemical Resistant
- Good Flow
- Good Moldability
- Odorless
- HIGHLIGHTS
DAI EL G - 8002L is a peroxide curable copolymer of vinylidene fluoride and hexafluoropropylene which provides excellent mold flow. It is suitable for extrusion and injection molding.. It provides superior chemical resistance compared with bisphenol curable products.
- Packing Specification
- 20 Kg
- Plastics and Elastomers End Uses
- O Rings
- Turbo Charger Hose
- Safety Information
Be sure to read the notes on SDS and labels before use.. This product is intended for general industry, and therefore its adequacy and safety as a raw material for medical purposes cannot be guaranteed.
- Plastics and Elastomers Processing Methods
- Extrusion
- Injection Molding
Technical data
Table 1 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Fluorine Content | 69 | mass% | — |
| Mooney Viscosity (ML₁₊₁₀) (at 100°C) | 33 | MU | ASTM D1646 |
| Mooney Viscosity (ML₁₊₁₀) (at 121°C) | 15 | MU | ASTM D1646 |
| Specific Gravity (at 23°C) | 1.81 | — | ASTM D792 |
Table 2 of 3
1 row| Characteristic | Value |
|---|---|
| Film Appearance | White to pale brown |
Table 3 of 3
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| 100% Tensile Stress*² | 2 | MPa | ASTM D412 |
| Compression Set (at 200°C,70 hours, 25% Compression*³)*² | 23 | % | — |
| Elongation (at break)*² | 350 | % | ASTM D412 |
| Hardness (at 3sec)*² | 63 | Shore A | ASTM D2240 |
| Hardness (at peak)*² | 66 | Shore A | ASTM D2240 |
| Low Temperature Retraction (TR10)*² | -13 | °C | ASTM D1329 |
| Tensile Strength*² | 22 | MPa | ASTM D412 |