DAI-EL G-565
- Chemical Family
- Fluoropolymers
DAI-EL G-565 is a solid terpolymer consisting of vinylidene fluoride, tetrafluoroethylene, and hexafluoropropylene. Specifically designed for applications in the automotive and industrial sectors, this material excels in extrusion processability. Its primary attributes include remarkable fuel resistance, making it apt for automotive fuel lines, fuel hoses, and O-rings. Utilizing a chemical cure method, it stands out for its odorless nature and good processability.
Properties
- Physical Form
- Solid
Product families
Applications
- Fuel Systems
- Powertrain & UTH
- Equipment & Parts
Product Families
- Fluoroelastomers
Other characteristics
- Brand
- DAI-EL
- Features
- Fuel Resistant, Good Processability, Odorless
- Polymer Name
- Fluoroelastomer (FKM)
- Processing Methods
- Extrusion
- Note
The above values in properties are representative and not guaranteed.. * [Formula] DAI EL G 565: 100 phr, SRF carbon black (N774): 13 phr, Calcium hydroxide: 6 phr, Magnesium Oxide high active): 3 phr, [Curing condition] Press cure: 45min at 160°C.
- Markets
- Automotive & Transportation
- Industrial
- Soluble In
- Lower ketones and esters
- Cure
- Chemical Cure
- Technology
- Elastomers
- Material Features
- Fuel Resistant
- Good Processability
- Odorless
- HIGHLIGHTS
DAI EL G - 565 is a bisphenol type cure incorporated terpolymer of vinylidene fluoride, tetrafluoroethylene and hexafluoropropylene which has excellent extrusion processability.. It offers excellent fuel resistance and is suitable for fuel hoses.
- Packing Specification
- 20 Kg
- Plastics and Elastomers End Uses
- Automotive Fuel Lines
- Fuel Hose
- O Rings
- Safety Information
Be sure to read the notes on SDS and labels before use.. This product is intended for general industry, and therefore its adequacy and safety as a raw material for medical purposes cannot be guaranteed.
- Plastics and Elastomers Processing Methods
- Extrusion
Technical data
Table 1 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Fluorine Content | 69 | mass% | — |
| Mooney Viscosity (ML₁₊₁₀) (at 100°C) | 39 | MU | ASTM D1646 |
| Mooney Viscosity (ML₁₊₁₀) (at 121°C) | 27 | MU | ASTM D1646 |
| Specific Gravity (at 23°C) | 1.87 | — | ASTM D792 |
Table 2 of 3
1 row| Characteristic | Value |
|---|---|
| Film Appearance | Milky white to pale yellow |
Table 3 of 3
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| 100% Tensile Stress*² | 2.2 | MPa | ASTM D412 |
| Elongation (at break)*² | 400 | % | ASTM D412 |
| Hardness (at 3sec)*² | 58 | Shore A | ASTM D2240 |
| Hardness (at peak)*² | 68 | Shore A | ASTM D2240 |
| Low Temperature Retraction (TR10)*² | -13 | °C | ASTM D1329 |
| Tensile Strength*² | 11.4 | MPa | ASTM D412 |