DAI-EL G-562
- Chemical Family
- Fluoropolymers
DAI-EL G-562 is a cure-incorporated terpolymer combining vinylidene fluoride, tetrafluoroethylene, and hexafluoropropylene, specifically designed for compression molding. This material excels in elongation at break and demonstrates robust adhesion to metal surfaces. It presents a harmonious blend of chemical resistance with low-temperature flexibility. Targeting the automotive, transportation, and industrial sectors, particularly powertrain, UTH, and equipment and parts, it finds prime applications in automotive fuel lines, fuel hoses, and O rings.
Properties
- Physical Form
- Sheets
- Solid
Product families
Applications
- Fuel Systems
- Powertrain & UTH
- Equipment & Parts
Product Families
- Fluoroelastomers
Other characteristics
- Brand
- DAI-EL
- Features
Chemical Resistant, Good Adhesion, Good Elongation, Low Temperature Flexibility, Odorless
- Polymer Name
- Fluoroelastomer (FKM)
- Note
*¹ The above values are representative and not guaranteed.; *2 [Formula] DAI-EL G-562: 100 phr, MT carbon black (N990): 20 phr, Calcium hydroxide: 6 phr, Magnesium Oxide (high-active): 3 phr, [Curing condition] Press cure: 10min at 170°C, Post cure: 24hrs at 230°C.; *3 P-24 O-ring.
- Markets
- Automotive & Transportation
- Industrial
- Soluble In
- Lower ketones and esters
- Technology
- Elastomers
- Material Features
- Chemical Resistant
- Good Adhesion
- Good Elongation
- Low Temperature Flexibility
- Odorless
- HIGHLIGHTS
DAI-EL G-562 is a cure-incorporated terpolymer of vinylidene fluoride, tetrafluoroethylene and hexafluoropropylene which is suitable for compression molding.; It offers excellent elongation at break and adhesion to metal .; It provides a good balance of chemical resistance and cold temperature flexibility.
- Packing Specification
- 20 Kg
- Safety Information
Be sure to read the Safety Data Sheet (SDS) and precautions on the label before using.. This product has been developed for industrial purposes and we shall not guarantee the safety if used for any other purposes. If it is going to be used for medical or food applications, please contact us in advance.
- Plastics and Elastomers End Uses
- Automotive Fuel Lines
- Fuel Hose
- O Rings
Technical data
Table 1 of 2
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Fluorine Content | 68.5 | mass% | — |
| Mooney Viscosity (ML₁₊₁₀) (at 100°C) | 77 | MU | ASTM D1646 |
| Mooney Viscosity (ML₁₊₁₀) (at 121°C) | 47 | MU | ASTM D1646 |
| Specific Gravity (at 23°C) | 1.87 | — | ASTM D792 |
Table 2 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| 100% Tensile Stress*² | 2.6 | MPa | ASTM D412 |
| Compression Set (at 200°C,70 hours, 25% Compression*³)*² | 40 | % | — |
| Elongation (at break)*² | 330 | % | ASTM D412 |
| Hardness (at 3sec)*² | 64 | Shore A | ASTM D2240 |
| Hardness (at peak)*² | 71 | Shore A | ASTM D2240 |
| Low Temperature Retraction (TR10)*² | -14 | °C | ASTM D1329 |
| Tensile Strength*² | 14.7 | MPa | ASTM D412 |