DAI-EL G-797
- Chemical Family
- Fluoropolymers
DAI-EL G-797 offers sheets with good mechanical properties, an odorless nature, and excellent fluidity. Colored yellow, it finds applications in the automotive and transportation markets, specifically in O rings and fuel entrance cover seals. Available in both powder and solid forms, these sheets have a characteristic appearance of white powder and are soluble in lower ketones and esters.
Properties
- Physical Form
- Sheets
Product families
- Powertrain & UTH
- Equipment & Parts
Other characteristics
- Brand
- DAI-EL
- Color
- Yellow
- End Uses
- Fuel Entrance Cover Seal, O Rings
- Features
Good Fluidity, Good Mechanical Properties, Odorless
- Polymer Name
- Fluoroelastomer (FKM)
- Tensile Strength
- 15.2 - 15.2 MPa
- Note
*1 The above values are representative and not guaranteed. *2 [Formula] DAI-EL G-797: 100 phr, MT carbon black (N990): 20 phr, Calcium hydroxide: 6 phr, Magnesium Oxide (high-active): 3 phr, [Curing condition] Press cure: 10min@170°C, Post cure: 24hrs@230°C. *3 P-24 O-ring.
- Markets
- Automotive & Transportation
- Industrial
- Soluble In
- Lower ketones and esters
- Technology
- Elastomers
- Benefits
DAI-EL G-797 is a cure-incorporated copolymer of vinylidene fluoride and hexafluoropropylene which is suitable for compression molding.. It provides excellent fluidity of molding and mechanical properties
- Product Families
- Elastomers — Parts & Shapes
- Material Features
- Good Fluidity
- Good Mechanical Properties
- Odorless
- Packing Specification
- 20Kg
- Plastics and Elastomers End Uses
- Fuel Entrance Cover Seal
- O Rings
- Safety Information
Be sure to read the Safety Data Sheet (SDS) and precautions on the label before using.. This product has been developed for industrial purpose and we shall not guarantee the safety if used for any other purposes. If it is going to be used for medical or food applications, please contact us in advance.
- Plastics and Elastomers Processing Methods
- Compression Molding
Technical data
Table 1 of 2
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Compression Set (at 200°C,70 hours, 25% Compression*³) | 22 | % | — |
| Elongation (at break) | 270 | % | ASTM D412 |
| Fluorine Content | 66 | mass% | — |
| Hardness (at 3 sec) | 64 | Shore A | ASTM D2240 |
| Hardness (at Peak) | 69 | Shore A | ASTM D2240 |
| Low Temperature Retraction (TR10) | -18 | °C | ASTM D1329 |
| Mooney Viscosity (ML₁₊₁₀) (at 100°C) | 47 | MU | ASTM D1646 |
| Mooney Viscosity (ML₁₊₁₀) (at 121°C) | 25 | MU | ASTM D1646 |
| Specific Gravity (at 23°C) | 1.81 | — | ASTM D792 |
| Tensile Strength | 15.2 | MPa | ASTM D412 |
Table 2 of 2
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| 100% Tensile Stress*² | 3.4 | MPa | ASTM D412 |