DAI-EL G-962
- Chemical Family
- Fluoropolymers
DAI-EL G-962 provides sheets with steam resistance, chemical resistance, and good mechanical properties. With a white color, it finds applications in O rings and turbocharger hoses within the automotive and transportation markets. The sheets, available in powder form, are soluble in lower ketones and esters.
Properties
- Physical Form
- Sheets
Product families
- Cooling & Climate
- Powertrain & UTH
- Equipment & Parts
Other characteristics
- Brand
- DAI-EL
- Color
- White
- End Uses
- O Rings, Turbo Charger Hose
- Features
Acid Resistant, Chemical Resistant, Good Mechanical Properties, Low Temperature Flexibility, Odorless, Steam Resistant
- Polymer Name
- Fluoroelastomer (FKM)
- Tensile Strength
- 18.0 - 18.0 MPa
- Note
*1 The above values are representative and not guaranteed.; *2 [Formula] DAI EL G 962: 100 phr, MT carbon black (N990): 20 phr, Triallylisocyanurate (100% active): 4 phr, 2,5 dimethyl 2,5 di(t butylperoxy)hexane (100% active): 1.5 phr, [Curing condition] Press cure: 10min@160°C, Post cure: 4hrs@180°C.; *3 P 24 O ring.
- Markets
- Automotive & Transportation
- Industrial
- Soluble In
- Lower ketones and esters
- Technology
- Elastomers
- Benefits
DAI EL G 962 is a peroxide curable terpolymer of vinylidene fluoride, tetrafluoroethylene and hexafluoropropylene which is suitable for injection molding.. It provides excellent mechanical properties and resistance to steam and acids and a good balance of chemical resistance and low temperature flexibility.
- Product Families
- Elastomers — Parts & Shapes
- Material Features
- Acid Resistant
- Chemical Resistant
- Good Mechanical Properties
- Low Temperature Flexibility
- Odorless
- Steam Resistant
- Packing Specification
- 20kg
- Plastics and Elastomers End Uses
- O Rings
- Turbo Charger Hose
- Safety Information
Be sure to read the notes on SDS and labels before use.. This product is intended for general industry, and therefore its adequacy and safety as a raw material for medical purposes cannot be guaranteed.
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 2
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Compression Set (at 200°C,70 hours, 25% Compression*³) | 17 | % | — |
| Fluorine Content | 67 | mass% | — |
| Elongation (at break) | 280 | % | ASTM D412 |
| Hardness (at 3 sec) | 63 | Shore A | ASTM D2240 |
| Hardness (at Peak) | 65 | Shore A | ASTM D2240 |
| Low Temperature Retraction (TR10) | -19 | °C | ASTM D1329 |
| Mooney Viscosity (ML₁₊₁₀) (at 100°C) | 47 | MU | ASTM D1646 |
| Mooney Viscosity (ML₁₊₁₀) (at 121°C) | 27 | MU | ASTM D1646 |
| Specific Gravity (at 23°C) | 1.83 | — | ASTM D792 |
| Tensile Strength | 18 | MPa | ASTM D412 |
Table 2 of 2
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| 100% Tensile Stress*² | 2.6 | MPa | ASTM D412 |