DAI-EL G-763F
- Chemical Family
- Fluoropolymers
DAI-EL G-763F, in solid form, features good processability and adhesion and is odorless. Targeting automotive and industrial applications, it serves in fuel entrance cover seals and O rings. Soluble in lower ketones and esters, this product is suitable for compression molding processes.
Properties
- Physical Form
- Solid
Product families
Applications
- Powertrain & UTH
- Equipment & Parts
Product Families
- Fluoroelastomers
Other characteristics
- Brand
- DAI-EL
- Features
- Good Adhesion, Good Processability, Odorless
- Polymer Name
- Fluoroelastomer (FKM)
- Processing Methods
- Compression Molding
- Note
*1 The above values are representative and not guaranteed.; *2 [Formula] DAI-EL G-763F: 100 phr, MT carbon black (N990): 20 phr, Calcium hydroxide: 6 phr, Magnesium Oxide (high-active): 3 phr, [Curing condition] Press cure: 15min@170°C, Post cure: 24hrs@230°C.; *3 P-24 O-ring.
- Markets
- Automotive & Transportation
- Industrial
- Soluble In
- Lower ketones and esters
- Technology
- Elastomers
- Benefits
DAI-EL G-763F is a cure-incorporated copolymer of vinylidene fluoride and hexafluoropropylene which is suitable for compression molding.. It provides excellent roll mixing processability and adhesion to metal.
- Material Features
- Good Adhesion
- Good Processability
- Odorless
- Packing Specification
- 20Kg
- Plastics and Elastomers End Uses
- Fuel Entrance Cover Seal
- O Rings
- Safety Information
Be sure to read the Safety Data Sheet (SDS) and precautions on the label before using.. This product has been developed for industrial purpose and we shall not guarantee the safety if used for any other purposes. If it is going to be used for medical or food applications, please contact us in advance.
- Plastics and Elastomers Processing Methods
- Compression Molding
Technical data
Table 1 of 2
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Compression Set (at 200°C,70 hours, 25% Compression*³) | 23 | % | — |
| Elongation (at break) | 250 | % | ASTM D412 |
| Fluorine Content | 66 | mass% | — |
| Hardness (at 3 sec) | 64 | Shore A | ASTM D2240 |
| Hardness (at Peak) | 68 | Shore A | ASTM D2240 |
| Low Temperature Retraction (TR10) | -18 | °C | ASTM D1329 |
| Mooney Viscosity (ML₁₊₁₀) (at 100°C) | 53 | MU | ASTM D1646 |
| Mooney Viscosity (ML₁₊₁₀) (at 121°C) | 32 | MU | ASTM D1646 |
| Specific Gravity (at 23°C) | 1.81 | — | ASTM D792 |
| Tensile Strength | 14.2 | MPa | ASTM D412 |
Table 2 of 2
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| 100% Tensile Stress*² | 3.2 | MPa | ASTM D412 |